This specification covers a gold-palladium-nickel alloy in the form of wire, rod, sheet, strip, foil, pig, powder, shot, and chips and a viscous mixture (paste) of powder in a suitable binder. This filler metal has been used typically for joining corrosion and heat resistant steels and alloys where corrosion and oxidation resistant joints with good strength at elevated temperatures are required, but usage is not limited to such applications.
SAE AMS4784G-2012 history
2018SAE AMS4784G-2018 Gold-Palladium-Nickel Alloy, Brazing Filler Metal, High Temperature 50Au - 25Pd - 25Ni 2015 to 2050 °F (1102 to 1121 °C) Solidus-Liquidus Range
2012SAE AMS4784G-2012 Gold-Palladium-Nickel Alloy, Brazing Filler Metal, High Temperature 50Au - 25Pd - 25Ni 2015 to 2050 °F (1102 to 1121 °C) Solidus-Liquidus Range (UNS P00500)
2006SAE AMS4784F-2006 Gold-Palladium-Nickel Alloy, Brazing Filler Metal, High Temperature 50Au - 25Pd - 25Ni 2015 to 2050 °F (1102 to 1121 °C) Solidus-Liquidus Range
2001SAE AMS4784F-2001 Gold-Palladium-Nickel Alloy@ Brazing Filler Metal@ High Temperature 50Au - 25Pd - 25Ni 2015 to 2050 °F (1102 to 1121 °C) Solidus-Liquidus Range (UNS P00500)
1999SAE AMS4784E-1999 Gold-Palladium-Nickel Alloy@ Brazing Filler Metal@ High Temperature 50Au - 25Pd - 25Ni 2015 to 2050 Degrees F (1102 to 1121 Degrees C) Solidus-Liquidus Range (UNS P00500)
1999SAE AMS4784D-1999 GOLD-PALLADIUM-NICKEL ALLOY BRAZING FILLER METAL, HIGH TEMPERATURE 50Au - 25Pd - 25Ni 2015 to 2050 °F (1102 to 1121°C) Solidus-Liquidus Range
1992SAE AMS4784D-1992 Gold-Palladium-Nickel Alloy Brazing Filler Metal@ High Temperature 50Au - 25Pd - 25Ni 2015 to 2050 Degrees F (1102 to 1121 Degrees C) Solidus-Liquidus Range
1990SAE AMS4784C-1990 BRAZING FILLER METAL@ HIGH TEMPERATURE 50Au - 25Pd - 25Ni@ 2015° - 2050°F (1102° - 1121°C) Solidus-Liquidus Range (UNS P00500)
1984SAE AMS4784B-1984 BRAZING FILLER METAL@ HIGH TEMPERATURE 50Au - 25Pd - 25Ni@ 2015° - 2050°F (1100° to 1120 °C) Solidus-Liquidus Range (UNS P00500)