SAE AMS4784F-2001
Gold-Palladium-Nickel Alloy@ Brazing Filler Metal@ High Temperature 50Au - 25Pd - 25Ni 2015 to 2050 °F (1102 to 1121 °C) Solidus-Liquidus Range (UNS P00500)

Standard No.

SAE AMS4784F-2001

Release Date

2001

Published By

SAE - SAE International

Status

Be replaced

Replace By

SAE AMS4784F-2006

Latest

SAE AMS4784G-2018

Scope

Form:This specification covers a gold-palladium-nickel alloy in the form of wire@ rod@ sheet@ strip@ foil@ pig@ powder@ shot@ chips@ preforms@ and a viscous mixture (paste) of the powder in a suitable binder.Application:This filler metal has been used typically for joining corrosion and heat-resistant steels and alloys where corrosion and oxidation-resistant joints with good strength at elevated temperatures are required@ but usage is not limited to such applications.Classifications:Filler metal supplied to this specification is classified as follows:Class 1 Standard compositionClass 2 Supplementary composition controlWhere no class is specified@ Class 1 shall apply.

SAE AMS4784F-2001 history

• 2018 SAE AMS4784G-2018 Gold-Palladium-Nickel Alloy, Brazing Filler Metal, High Temperature 50Au - 25Pd - 25Ni 2015 to 2050 °F (1102 to 1121 °C) Solidus-Liquidus Range
• 2012 SAE AMS4784G-2012 Gold-Palladium-Nickel Alloy, Brazing Filler Metal, High Temperature 50Au - 25Pd - 25Ni 2015 to 2050 °F (1102 to 1121 °C) Solidus-Liquidus Range (UNS P00500)
• 2006 SAE AMS4784F-2006 Gold-Palladium-Nickel Alloy, Brazing Filler Metal, High Temperature 50Au - 25Pd - 25Ni 2015 to 2050 °F (1102 to 1121 °C) Solidus-Liquidus Range
• 2001 SAE AMS4784F-2001 Gold-Palladium-Nickel Alloy@ Brazing Filler Metal@ High Temperature 50Au - 25Pd - 25Ni 2015 to 2050 °F (1102 to 1121 °C) Solidus-Liquidus Range (UNS P00500)
• 1999 SAE AMS4784E-1999 Gold-Palladium-Nickel Alloy@ Brazing Filler Metal@ High Temperature 50Au - 25Pd - 25Ni 2015 to 2050 Degrees F (1102 to 1121 Degrees C) Solidus-Liquidus Range (UNS P00500)
• 1999 SAE AMS4784D-1999 GOLD-PALLADIUM-NICKEL ALLOY BRAZING FILLER METAL, HIGH TEMPERATURE 50Au - 25Pd - 25Ni 2015 to 2050 °F (1102 to 1121°C) Solidus-Liquidus Range
• 1992 SAE AMS4784D-1992 Gold-Palladium-Nickel Alloy Brazing Filler Metal@ High Temperature 50Au - 25Pd - 25Ni 2015 to 2050 Degrees F (1102 to 1121 Degrees C) Solidus-Liquidus Range
• 1990 SAE AMS4784C-1990 BRAZING FILLER METAL@ HIGH TEMPERATURE 50Au - 25Pd - 25Ni@ 2015° - 2050°F (1102° - 1121°C) Solidus-Liquidus Range (UNS P00500)
• 1984 SAE AMS4784B-1984 BRAZING FILLER METAL@ HIGH TEMPERATURE 50Au - 25Pd - 25Ni@ 2015° - 2050°F (1100° to 1120 °C) Solidus-Liquidus Range (UNS P00500)
• 1978 SAE AMS4784A-1978 BRAZING FILLER METAL@ HIGH TEMPERATURE@ 50Au - 25Pd - 25Ni@ 2015° - 2050°F (1100° - 1120°C) Solidus-Liquidus Range (UNS P00500)
• 1968 SAE AMS4784-1968 BRAZING FILLER METAL@ HIGH TEMPERATURE 50 Au - 25Pd - 25Ni