SAE AMS4784E-1999 Gold-Palladium-Nickel Alloy@ Brazing Filler Metal@ High Temperature 50Au - 25Pd - 25Ni 2015 to 2050 Degrees F (1102 to 1121 Degrees C) Solidus-Liquidus Range (UNS P00500)
2018SAE AMS4784G-2018 Gold-Palladium-Nickel Alloy, Brazing Filler Metal, High Temperature 50Au - 25Pd - 25Ni 2015 to 2050 °F (1102 to 1121 °C) Solidus-Liquidus Range
2012SAE AMS4784G-2012 Gold-Palladium-Nickel Alloy, Brazing Filler Metal, High Temperature 50Au - 25Pd - 25Ni 2015 to 2050 °F (1102 to 1121 °C) Solidus-Liquidus Range (UNS P00500)
2006SAE AMS4784F-2006 Gold-Palladium-Nickel Alloy, Brazing Filler Metal, High Temperature 50Au - 25Pd - 25Ni 2015 to 2050 °F (1102 to 1121 °C) Solidus-Liquidus Range
2001SAE AMS4784F-2001 Gold-Palladium-Nickel Alloy@ Brazing Filler Metal@ High Temperature 50Au - 25Pd - 25Ni 2015 to 2050 °F (1102 to 1121 °C) Solidus-Liquidus Range (UNS P00500)
1999SAE AMS4784E-1999 Gold-Palladium-Nickel Alloy@ Brazing Filler Metal@ High Temperature 50Au - 25Pd - 25Ni 2015 to 2050 Degrees F (1102 to 1121 Degrees C) Solidus-Liquidus Range (UNS P00500)
1999SAE AMS4784D-1999 GOLD-PALLADIUM-NICKEL ALLOY BRAZING FILLER METAL, HIGH TEMPERATURE 50Au - 25Pd - 25Ni 2015 to 2050 °F (1102 to 1121°C) Solidus-Liquidus Range
1992SAE AMS4784D-1992 Gold-Palladium-Nickel Alloy Brazing Filler Metal@ High Temperature 50Au - 25Pd - 25Ni 2015 to 2050 Degrees F (1102 to 1121 Degrees C) Solidus-Liquidus Range
1990SAE AMS4784C-1990 BRAZING FILLER METAL@ HIGH TEMPERATURE 50Au - 25Pd - 25Ni@ 2015° - 2050°F (1102° - 1121°C) Solidus-Liquidus Range (UNS P00500)
1984SAE AMS4784B-1984 BRAZING FILLER METAL@ HIGH TEMPERATURE 50Au - 25Pd - 25Ni@ 2015° - 2050°F (1100° to 1120 °C) Solidus-Liquidus Range (UNS P00500)