SAE AMS2515B-1965 PDF

Scope: APPLICATION: Primarily as a coating on metal parts to produce a fused polytetrafluoroethylene resin surface providing dry lubrication@ high heat stability@ and good corrosion protection. Applicable primarily to parts which operate at temperatures not higher than 525 F (274 C) for limited periods or 475 F (246 C) for extended periods. The preheating temperature for steels and the fusing temperature may result in some softening of metals which have been cold worked or have been given final heat treatment at temperatures lower than these temperatures.

SAE AMS2515B-1965 history

2018 SAE AMS2515H-2018 Polytetrafluoroethylene (PTFE) Resin Coating@ Low Build@ 370 to 400 °C (698 to 752 °F) Fusion
2013 SAE AMS2515G-2013 Polytetrafluoroethylene (PTFE) Resin Coating, Low Build, 370 to 400°C (698 to 752°F) Fusion
2011 SAE AMS2515F-2011 Polytetrafluoroethylene (PTFE) Resin Coating, Low Build, 370 to 400°C (698 to 752°F) Fusion
2003 SAE AMS2515E-2003 Polytetrafluoroethylene (PTFE) Resin Coating Low Build, 370 to 400 °C (698 to 752 °F) Fusion
2003 SAE AMS2515D-2003 Polytetrafluoroethylene (PTFE) Resin Coating Low Build, 370 to 400 °C (698 to 752 °F) Fusion
1990 SAE AMS2515E-1990 Polytetrafluoroethylene (PTFE) Resin Coating Low Build, 370 - 400 Degrees C (698 - 752 Degrees F) Fusion
1983 SAE AMS2515D-1983 Polytetrafluoroethylene Resin Coating Low Build@ 370 Degrees - 400 Degrees C (700 Degrees - 750 Degrees F) Fusion
1974 SAE AMS2515C-1974 Polytetrafluoroethylene Resin Coating Low Build@ 700 Degrees - 750 Degrees F (371 Degrees - 399 Degrees C) Fusion
1965 SAE AMS2515B-1965 Polytetrafluoroethylene Resin Coating Low Build@ 700 - 750 F (371 - 399 C) Fusion
1963 SAE AMS2515A-1963 Polytetrafluoroethylene Resin Coating Low Build@ 700 - 750 F (370 - 400 C) Fusion
1961 SAE AMS2515-1961 Polytetrafluoroethylene Resin Coating 700 - 750 F Fusion