ASTM B695-04(2016)
Standard Specification for Coatings of Zinc Mechanically Deposited on Iron and Steel
- Standard No.
- ASTM B695-04(2016)
- Release Date
- 2004
- Published By
- American Society for Testing and Materials (ASTM)
- Status
- Replace By
- ASTM B695-21
- Latest
- ASTM B695-21
- Scope
1.1 This specification covers the requirements for a coating of zinc mechanically deposited on iron and steel basis metals. The coating is provided in several thicknesses up to and including 107 μm. The seven thickest classes are usually referred to as “mechanically galvanized.”
1.2 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
Note 1: The performance of this coating complies with the requirements of Specification A153/A153M and MIL-C-81562.
1.3 The values stated in SI units are to be regarded as the standard. The inch-pound equivalents of SI units are given for informational purposes.
ASTM B695-04(2016) Referenced Document
- ASTM A153/A153M Standard Specification for Zinc Coating (Hot-Dip) on Iron and Steel Hardware
- ASTM A194/A194M Standard Specification for Carbon and Alloy Steel Nuts for Bolts for High Pressure or High Temperature Service, or Both
- ASTM A325 Standard Specification for High-Strength Bolts For Structural Steel Joints
- ASTM A490 Standard Specification for Quenched And Tempered Alloy Steel Bolts For Structural Steel Joints
- ASTM A563 Standard Specification for Carbon and Alloy Steel Nuts*， 2024-04-20 Update
- ASTM B117 Standard Practice for Operating Salt Spray (Fog) Apparatus
- ASTM B183 Standard Practice for Preparation of Low-Carbon Steel for Electroplating
- ASTM B242 Standard Guide for Preparation of High-Carbon Steel for Electroplating
- ASTM B322 Standard Guide for Cleaning Metals Prior to Electroplating
- ASTM B487 Standard Test Method for Measurement of Metal and Oxide Coating Thickness by Microscopical Examination of Cross Section
- ASTM B499 Standard Test Method for Measurement of Coating Thicknesses by the Magnetic Method: Nonmagnetic Coatings on Magnetic Basis Metals
- ASTM B571 Standard Practice for Qualitative Adhesion Testing of Metallic Coatings
- ASTM B602 Standard Test Method for Attribute Sampling of Metallic and Inorganic Coatings
- ASTM B697 Standard Guide for Selection of Sampling Plans for Inspection of Electrodeposited Metallic and Inorganic Coatings
- ASTM B762 Standard Test Method of Variables Sampling of Metallic and Inorganic Coatings
- ASTM F1470 Standard Practice for Fastener Sampling for Specified Mechanical Properties and Performance Inspection
ASTM B695-04(2016) history
- 2021 ASTM B695-21 Standard Specification for Coatings of Zinc Mechanically Deposited on Iron and Steel
- 2004 ASTM B695-04(2016) Standard Specification for Coatings of Zinc Mechanically Deposited on Iron and Steel
- 2004 ASTM B695-04(2009) Standard Specification for Coatings of Zinc Mechanically Deposited on Iron and Steel
- 2004 ASTM B695-04 Standard Specification for Coatings of Zinc Mechanically Deposited on Iron and Steel
- 2000 ASTM B695-00 Standard Specification for Coatings of Zinc Mechanically Deposited on Iron and Steel