ASTM B695-04(2009)
Standard Specification for Coatings of Zinc Mechanically Deposited on Iron and Steel
- Standard No.
- ASTM B695-04(2009)
- Release Date
- 2004
- Published By
- American Society for Testing and Materials (ASTM)
- Status
- Replace By
- ASTM B695-04(2016)
- Latest
- ASTM B695-21
- Scope
1.1 This specification covers the requirements for a coating of zinc mechanically deposited on iron and steel basis metals. The coating is provided in several thicknesses up to and including 107 μm. The seven thickest classes are usually referred to as “mechanically galvanized.”
1.2 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
Note 18212;The performance of this coating complies with the requirements of Specification A153/A153M and MIL-C-81562.
1.3 The values stated in SI units are to be regarded as the standard. The inch-pound equivalents of SI units are given for informational purposes.
ASTM B695-04(2009) Referenced Document
- ASTM A153/A153M Standard Specification for Zinc Coating (Hot-Dip) on Iron and Steel Hardware
- ASTM A194/A194M Standard Specification for Carbon and Alloy Steel Nuts for Bolts for High Pressure or High Temperature Service, or Both
- ASTM A325 Standard Specification for High-Strength Bolts For Structural Steel Joints
ASTM B695-04(2009) history
- 2021 ASTM B695-21 Standard Specification for Coatings of Zinc Mechanically Deposited on Iron and Steel
- 2004 ASTM B695-04(2016) Standard Specification for Coatings of Zinc Mechanically Deposited on Iron and Steel
- 2004 ASTM B695-04(2009) Standard Specification for Coatings of Zinc Mechanically Deposited on Iron and Steel
- 2004 ASTM B695-04 Standard Specification for Coatings of Zinc Mechanically Deposited on Iron and Steel
- 2000 ASTM B695-00 Standard Specification for Coatings of Zinc Mechanically Deposited on Iron and Steel