DIN EN ISO 16151:2018
Corrosion of metals and alloys - Accelerated cyclic test with exposure to acidified salt spray, dry and wet conditions (ISO 16151:2018); German version EN ISO 16151:2018

Standard No.

DIN EN ISO 16151:2018

Release Date

2018

Published By

German Institute for Standardization

Status

Be replaced

Replace By

DIN EN ISO 16151:2018-10

Latest

DIN EN ISO 16151:2018-10

Replace

DIN EN ISO 16151:2008 DIN EN ISO 16151:2017

Scope

This document specifies two accelerated corrosion-test procedures, Methods A and B, for the comparative evaluation of metallic materials with or without permanent corrosion protection or temporary corrosion protection in outdoor salt/acid rain environments. It also specifies the apparatus used. The two tests involve cyclic exposure of the specimens to acidified salt spray, "dry" and "wet" conditions.

DIN EN ISO 16151:2018 Referenced Document

• DIN EN ISO 10289:2001 Methods for corrosion testing of metallic and other inorganic coatings on metallic substrates - Rating of test specimens and manufactured articles subjected to corrosion tests (ISO 10289:1999); German version EN ISO 10289:2001
• DIN EN ISO 11130:2018 Corrosion of metals and alloys - Alternate immersion test in salt solution (ISO 11130:2017); German version EN ISO 11130:2018
• DIN EN ISO 1514:2016 Paints and varnishes - Standard panels for testing (ISO 1514:2016); German version EN ISO 1514:2016
• DIN EN ISO 17872:2007 Paints and varnishes - Guidelines for the introduction of scribe marks through coatings on metallic panels for corrosion testing (ISO 17872:2007);English version of DIN EN ISO 17872:2007-06
• DIN EN ISO 2808:2007 Paints and varnishes - Determination of film thickness (ISO 2808:2007) English version of DIN EN ISO 2808:2007-05
• DIN EN ISO 4623-2:2016 Paints and varnishes - Determination of resistance to filiform corrosion - Part 2: Aluminium substrates (ISO 4623-2:2016); German version EN ISO 4623-2:2016
• DIN EN ISO 4628-1:2016 Paints and varnishes - Evaluation of degradation of coatings - Designation of quantity and size of defects, and of intensity of uniform changes in appearance - Part 1: General introduction and designation system (ISO 4628-1:2016); German version EN ISO 46
• DIN EN ISO 4628-2:2016 Paints and varnishes - Evaluation of degradation of coatings - Designation of quantity and size of defects, and of intensity of uniform changes in appearance - Part 2: Assessment of degree of blistering (ISO 4628-2:2016); German version EN ISO 4628-2:2016*， 2024-04-20 Update
• DIN EN ISO 4628-3:2016 Paints and varnishes - Evaluation of degradation of coatings - Designation of quantity and size of defects, and of intensity of uniform changes in appearance - Part 3: Assessment of degree of rusting (ISO 4628-3:2016); German version EN ISO 4628-3:2016
• DIN EN ISO 4628-4:2016 Paints and varnishes - Evaluation of degradation of coatings - Designation of quantity and size of defects, and of intensity of uniform changes in appearance - Part 4: Assessment of degree of cracking (ISO 4628-4:2016); German version EN ISO 4628-4:2016
• DIN EN ISO 4628-5:2016 Paints and varnishes - Evaluation of degradation of coatings - Designation of quantity and size of defects, and of intensity of uniform changes in appearance - Part 5: Assessment of degree of flaking (ISO 4628-5:2016); German version EN ISO 4628-5:2016
• DIN EN ISO 4628-8:2013 Paints and varnishes - Evaluation of degradation of coatings - Designation of quantity and size of defects, and of intensity of uniform changes in appearance - Part 8: Assessment of degree of delamination and corrosion around a scribe or other artificial
• DIN EN ISO 8044:2015 Corrosion of metals and alloys - Basic terms and definitions (ISO 8044:2015); Trilingual version EN ISO 8044:2015
• DIN EN ISO 8407:2014 Corrosion of metals and alloys - Removal of corrosion products from corrosion test specimens (ISO 8407:2009); German version EN ISO 8407:2014
• DIN EN ISO 8993:2010 Anodizing of aluminium and its alloys - Rating system for the evaluation of pitting corrosion - Chart method (ISO 8993:2010); German version EN ISO 8993:2010
• DIN EN ISO 9227:2017 Corrosion tests in artificial atmospheres - Salt spray tests (ISO 9227:2017); German version EN ISO 9227:2017
• ISO 11130:2017 Corrosion of metals and alloys - Alternate immersion test in salt solution
• ISO 1514:2016 Paints and varnishes - Standard panels for testing
• ISO 17872:2007 Paints and varnishes - Guidelines for the introduction of scribe marks through coatings on metallic panels for corrosion testing
• ISO 2808:2007 Paints and varnishes - Determination of film thickness
• ISO 3574:2012 Cold-reduced carbon steel sheet of commercial and drawing qualities
• ISO 4623-2:2016 Paints and varnishes - Determination of resistance to filiform corrosion - Part 2: Aluminium substrates
• ISO 8044:2015 Corrosion of metals and alloys - Basic terms and definitions

DIN EN ISO 16151:2018 history

• 2018 DIN EN ISO 16151:2018-10 Corrosion of metals and alloys - Accelerated cyclic test with exposure to acidified salt spray, dry and wet conditions (ISO 16151:2018); German version EN ISO 16151:2018
• 2018 DIN EN ISO 16151:2018 Corrosion of metals and alloys - Accelerated cyclic test with exposure to acidified salt spray, dry and wet conditions (ISO 16151:2018); German version EN ISO 16151:2018
• 2008 DIN EN ISO 16151:2008 Corrosion of metals and alloys - Accelerated cyclic tests with exposure to acidified salt spray, "dry" and "wet" conditions (ISO 16151:2005); German version EN ISO 16151:2008
• 0000 DIN EN ISO 16151:2007