DIN EN ISO 16151:2008 Corrosion of metals and alloys - Accelerated cyclic tests with exposure to acidified salt spray, "dry" and "wet" conditions (ISO 16151:2005); German version EN ISO 16151:2008
This International Standard specifies two accelerated corrosion-test procedures, Methods A and B, for the
comparative evaluation of metallic materials with or without permanent corrosion protection or temporary
corrosion protection in outdoor salt/acid rain environments. It also specifies the apparatus used. The two tests
involve cyclic exposure of the specimens to acidified salt spray, "dry" and "wet" conditions.
The particular advantages of the two tests over conventional accelerated tests, such as the neutral salt spray
test (NSS) as specified in ISO 9227 lie in their better ability to reproduce the corrosion that occurs in outdoor
salt/acid rain environments. They are also useful for evaluating cosmetic corrosion.
Method A applies to
-- metals and their alloys,
-- metallic coatings (cathodic),
-- anodic oxide coatings, and
-- organic coatings on metallic materials.
Method B applies to
-- steel coated with anodic coatings, and
-- steel coated with anodic coatings covered with conversion coatings.
DIN EN ISO 16151:2008 Referenced Document
ISO 10289:1999 Methods for corrosion testing of metallic and other inorganic coatings on metallic substrates - Rating of test specimens and manufactured articles subjected to corrosion tests
ISO 11130:1999 Corrosion of metals and alloys - Alternate immersion test in salt solution
ISO 4628-1:2003 Paints and varnishes - Evaluation of degradation of coatings; Designation of quantity and size of defects, and of intensity of uniform changes in appearance - Part 1: General introduction and designation system
ISO 4628-2:2003 Paints and varnishes - Evaluation of degradation of coatings; Designation of quantity and size of defects, and of intensity of uniform changes in appearance - Part 2: Assessment of degree of blistering
ISO 4628-3:2003 Paints and varnishes - Evaluation of degradation of coatings; Designation of quantity and size of defects, and of intensity of uniform changes in appearance - Part 3: Assessment of degree of rusting
ISO 4628-4:2003 Paints and varnishes - Evaluation of degradation of coatings; Designation of quantity and size of defects, and of intensity of uniform changes in appearance - Part 4: Assessment of degree of cracking
ISO 4628-5:2003 Paints and varnishes - Evaluation of degradation of coatings; Designation of quantity and size of defects, and of intensity of uniform changes in appearance - Part 5: Assessment of degree of flaking
ISO 8407:1991 Corrosion of metals and alloys; removal of corrosion products from corrosion test specimens
ISO 8993:1989 Anodized aluminium and aluminium alloys; rating system for the evaluation of pitting corrosion; chart method
ISO 9227:1990 Corrosion tests in artificial atmospheres; salt spray tests
DIN EN ISO 16151:2008 history
2018DIN EN ISO 16151:2018-10 Corrosion of metals and alloys - Accelerated cyclic test with exposure to acidified salt spray, dry and wet conditions (ISO 16151:2018); German version EN ISO 16151:2018
2018DIN EN ISO 16151:2018 Corrosion of metals and alloys - Accelerated cyclic test with exposure to acidified salt spray, dry and wet conditions (ISO 16151:2018); German version EN ISO 16151:2018
2008DIN EN ISO 16151:2008 Corrosion of metals and alloys - Accelerated cyclic tests with exposure to acidified salt spray, "dry" and "wet" conditions (ISO 16151:2005); German version EN ISO 16151:2008