SAE AMS5412A-2012
Steel Castings, Vacuum Melted, Vacuum Cast, Investment, Corrosion Resistant 13Cr 8.0Ni 2.2Mo 1.1Al (195 psi) (1344 MPa) Tensile Strength (Condition H1000) Homogenized, Solution, Precipitation Heat Treated

Standard No.

SAE AMS5412A-2012

Release Date

2012

Published By

Society of Automotive Engineers (SAE)

Status

Be replaced

Replace By

SAE AMS5412A-2018

Latest

SAE AMS5412B-2019

Scope

This specification covers a corrosion-resistant steel in the form of investment castings. Primarily for parts requiring corrosion resistance and strength up to 600 °F (316 °C).

SAE AMS5412A-2012 Referenced Document

• ASTM A370-12 Standard Test Methods and Definitions for Mechanical Testing of Steel Products*， 2024-04-19 Update
• ASTM E192-04 Standard Reference Radiographs for Investment Steel Castings of Aerospace Applications*， 2024-04-19 Update
• SAE AMS-H-6875-1998 Heat Treatment of Steel, Process for
• SAE AMS2175-2003 Castings, Classification and Inspection of
• SAE AMS2635 RADIOGRAPHIC INSPECTION
• SAE AMS2640 MAGNETIC INSPECTION
• SAE AMS2645 Fluorescent Penetrant Inspection
• SAE AMS2694 REPAIR WELDING OF AEROSPACE CASTINGS
• SAE AMS2759 HEAT TREATMENT OF STEEL PARTS General Requirements
• SAE AMS2804 IDENTIFICATION Castings

SAE AMS5412A-2012 history

• 2019 SAE AMS5412B-2019 Steel Castings, Vacuum Melted, Vacuum Cast, Investment, Corrosion-Resistant 13Cr - 8.0Ni - 2.2Mo - 1.1Al 195 ksi (1344 MPa) Tensile Strength (Condition H1000) Homogenized, Solution, and Precipitation Heat Treated
• 2018 SAE AMS5412A-2018 Steel Castings, Vacuum Melted, Vacuum Cast, Investment, Corrosion-Resistant 13Cr - 8.0Ni - 2.2Mo - 1.1Al (195 ksi (1344 MPa) Tensile Strength (Condition H1000) Homogenized, Solution, and Precipitation Heat Treated
• 2012 SAE AMS5412A-2012 Steel Castings, Vacuum Melted, Vacuum Cast, Investment, Corrosion Resistant 13Cr 8.0Ni 2.2Mo 1.1Al (195 psi) (1344 MPa) Tensile Strength (Condition H1000) Homogenized, Solution, Precipitation Heat Treated
• 2007 SAE AMS5412-2007 Steel Castings, Vacuum Melted, Vacuum Cast, Investment, Corrosion Resistant 13Cr - 8.0Ni - 2.2Mo - 1.1Al (195,000 psi (1344 MPa) Tensile Strength (Condition H1000) Homogenized, Solution, and Precipitation Heat Treated
• 1990 SAE AMS5412-1990 Steel Castings, Vacuum Melted, Vacuum Cast, Investment, Corrosion Resistant 13Cr - 8.0Ni - 2.2Mo - 1.1Al (195,000 psi (1344 MPa) Tensile Strength (Condition H1000) Homogenized, Solution, and Precipitation Heat Treated UNS N13800