SAE AMS5412A-2018
Steel Castings, Vacuum Melted, Vacuum Cast, Investment, Corrosion-Resistant 13Cr - 8.0Ni - 2.2Mo - 1.1Al (195 ksi (1344 MPa) Tensile Strength (Condition H1000) Homogenized, Solution, and Precipitation Heat Treated

Standard No.

SAE AMS5412A-2018

Release Date

2018

Published By

Society of Automotive Engineers (SAE)

Status

Be replaced

Replace By

SAE AMS5412B-2019

Latest

SAE AMS5412B-2019

Scope

This specification covers a corrosion-resistant steel in the form of investment castings.

SAE AMS5412A-2018 history

• 2019 SAE AMS5412B-2019 Steel Castings, Vacuum Melted, Vacuum Cast, Investment, Corrosion-Resistant 13Cr - 8.0Ni - 2.2Mo - 1.1Al 195 ksi (1344 MPa) Tensile Strength (Condition H1000) Homogenized, Solution, and Precipitation Heat Treated
• 2018 SAE AMS5412A-2018 Steel Castings, Vacuum Melted, Vacuum Cast, Investment, Corrosion-Resistant 13Cr - 8.0Ni - 2.2Mo - 1.1Al (195 ksi (1344 MPa) Tensile Strength (Condition H1000) Homogenized, Solution, and Precipitation Heat Treated
• 2012 SAE AMS5412A-2012 Steel Castings, Vacuum Melted, Vacuum Cast, Investment, Corrosion Resistant 13Cr 8.0Ni 2.2Mo 1.1Al (195 psi) (1344 MPa) Tensile Strength (Condition H1000) Homogenized, Solution, Precipitation Heat Treated
• 2007 SAE AMS5412-2007 Steel Castings, Vacuum Melted, Vacuum Cast, Investment, Corrosion Resistant 13Cr - 8.0Ni - 2.2Mo - 1.1Al (195,000 psi (1344 MPa) Tensile Strength (Condition H1000) Homogenized, Solution, and Precipitation Heat Treated
• 1990 SAE AMS5412-1990 Steel Castings, Vacuum Melted, Vacuum Cast, Investment, Corrosion Resistant 13Cr - 8.0Ni - 2.2Mo - 1.1Al (195,000 psi (1344 MPa) Tensile Strength (Condition H1000) Homogenized, Solution, and Precipitation Heat Treated UNS N13800