1.1 This specification covers electric fusion welded pipe suitable for high-temperature or corrosive service as listed in Table 1. (Although no restrictions are placed on the sizes of pipe that may be furnished under this specification, commercial practice is commonly limited to sizes not less than 8 in. (203 mm) nominal diameter.)
1.2 Five classes of pipe are covered as follows:
1.2.1 Class 18212;Pipe shall be double welded by processes employing filler metal in all passes and shall be completely radiographed.
1.2.2 Class 28212;Pipe shall be double welded by processes employing filler metal in all passes. No radiography is required.
1.2.3 Class 38212;Pipe shall be single welded by processes employing filler metal in all passes and shall be completely radiographed.
1.2.4 Class 48212;Same as Class 3 except that the weld pass exposed to the inside pipe surface may be made without the addition of filler metal.
1.2.5 Class 58212;Pipe shall be double welded by processes employing filler metal in all passes and shall be spot radiographed.
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Material Safety Data Sheet (MSDS) for this product/material as provided by the manufacturer, to establish appropriate safety and health practices, and determine the applicability of regulatory limitations prior to use.
TABLE 1 Recommended Heat Treatment
| Alloy | UNS Designation | PWHTA, B Deg. F. (Deg. C) | Quench |
|---|---|---|---|
| 200 (Ni) | N02200 | 1650-1700 (900 to 928) | Rapid Air/water |
| 201 (Low C) | N02201 | 1650-1700 (900 to 928) | Rapid Air/water |
| 400 (Ni-Cu) | N04400 | 1650-1700 (900 to 928) | Rapid Air/water |
| X (Ni-Cr-Mo-Fe) | N06002 | 2150 (1177)C | Rapid Air/water |
| C22D (Low C-Ni-Mo-Cr) | N06022 | 2050-(1120)C | Rapid Air/water |
G30D (Ni-Cr-Fe-Mo-Cu)
ASTM B474-03(2009) history