ASTM A529/A529M-05
Standard Specification for High-Strength Carbon-Manganese Steel of Structural Quality

Standard No.

ASTM A529/A529M-05

Release Date

2005

Published By

American Society for Testing and Materials (ASTM)

Status

Be replaced

Replace By

ASTM A529/A529M-05(2009)

Latest

ASTM A529/A529M-19

Scope

1.1 This specification covers carbon-manganese steel shapes, plates, and bars of structural quality for use in riveted, bolted, or welded construction of buildings and for general structural purposes.

1.2 Material under this specification is available in two grades:

Grade Yield Strength,ksi [MPa] Thickness 50 [345] 50 [345] Plates to 1 in. [25 mm] thickto 14 in. [355 mm] wideBars to 31/2 in. [90 mm] Shapes with flange or leg thickness to 11/2 in. [40 mm] inclusive55 [380] 55 [380] Plates to 1 in. [25 mm] thick to 14 in. [355 mm] wideBars to 3 in. [75 mm] Shapes with flange or leg thickness to 11/2 in. [40 mm] inclusive

1.3 When the steel is to be welded, it is presupposed that a welding procedure suitable for the grade of steel and intended use or service will be utilized. See Appendix X3 of Specification A 6/A 6M for information on weldability.

1.4 The values stated in either inch-pound units or SI units are to be regarded as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other.

ASTM A529/A529M-05 history

• 2019 ASTM A529/A529M-19 Standard Specification for High-Strength Carbon-Manganese Steel of Structural Quality
• 2014 ASTM A529/A529M-14 Standard Specification for High-Strength Carbon-Manganese Steel of Structural Quality
• 2005 ASTM A529/A529M-05(2009) Standard Specification for High-Strength Carbon-Manganese Steel of Structural Quality
• 2005 ASTM A529/A529M-05 Standard Specification for High-Strength Carbon-Manganese Steel of Structural Quality
• 2004 ASTM A529/A529M-04 Standard Specification for High-Strength Carbon-Manganese Steel of Structural Quality
• 2003 ASTM A529/A529M-03 Standard Specification for High-Strength Carbon-Manganese Steel of Structural Quality
• 2002 ASTM A529/A529M-02 Standard Specification for High-Strength Carbon-Manganese Steel of Structural Quality
• 2001 ASTM A529/A529M-01 Standard Specification for High-Strength Carbon-Manganese Steel of Structural Quality
• 2000 ASTM A529/A529M-00 Standard Specification for High-Strength Carbon-Manganese Steel of Structural Quality
• 1975 ASTM A529-75 Standard Specification for Structural Steel With 42 000 Psi (290 Mpa) Minimum Yield Point (1/2 In. (12.7 Mm) Maximum Thickness)