This specifications covers a corrosion and moderate heat resistant steel in the form of bars,wire,forging,flash welded rings,and stock for forging or flash welded rings.Primarily for parts requriring corrosion resistance and high strength up to 600℉(315℃).
SAE AMS5739D-1987 history
2006SAE AMS5739E-2006 Steel@ Corrosion and Moderate Heat Resistant@ Bars@ Forgings@ and Rings 14.5Cr - 6.5Ni - 0.72Ti Solution Heat Treated and Maraged@ 180@000 psi (1240 MPa) Tensile Strength (UNS S36200)
2000SAE AMS5739D-2000 Steel, Corrosion and Moderate Heat Resistant, Bars, Forgings, and Rings 14.5Cr - 6.5Ni - 0.72Ti Solution Heat Treated and Maraged, 180,000 psi (1240 MPa) Tensile Strength
1991SAE AMS5739D-1991 Steel@ Corrosion and Moderate Heat Resistant@ Bars@ Forgings@ and Rings 14.5Cr - 6.5Ni - 0.72Ti Solution Heat Treated and Maraged@ 180@000 psi (1240 MPa) Tensile Strength (Reaf. Noncur. November 2000; UNS S36200)
1987SAE AMS5739D-1987 Steel, Corrosion and Moderate Heat Resistant, Bars, Forgings, and Rings, 14.5Cr 6.5Ni 0.72Ti, Solution Heat Treated and Maraged, 180,000 psi (1240 MPa) Tensile Strength
1987SAE AMS5739C-1987 STEEL BARS, FORGINGS, AND RINGS, CORROSION AND MODERATE HEAT RESISTANT 14.5Cr - 6.5Ni - 0.72Ti Solution Heat Treated and Maraged, 180,000 psi (1240 MPa) Tensile Strength
1981SAE AMS5739B-1981 STEEL BARS, FORGINGS, AND RINGS, CORROSION AND MODERATE HEAT RESISTANT 14.5Cr - 6.5Ni - 0.72Ti Solution Heat Treated and Maraged, 180,000 psi (1241 MPa) Tensile Strength
1974SAE AMS5739A-1974 STEEL BARS, FORGINGS, AND RINGS, CORROSION AND MODERATE HEAT RESISTANT 14.5Cr - 6.5Ni - 0.72Ti Solution Treated and Maraged, 180,000 psi (1241 MPa) Tensile Strength
1968SAE AMS5739-1968 STEEL BARS, FORGINGS, AND RINGS, CORROSION AND MODERATE HEAT RESISTANT 14.5Cr - 6.5Ni - 0.72Ti Solution Treated and Maraged (180,000 psi)