Form:This specification covers a corrosion and moderate heat resistant steel in the form of bars@ wire@ forging@ flash welded rings@ and stock for forging or flash welded rings.Application:Primarily for parts requiring corrosion resistance and high strength up to 600??(315??.
SAE AMS5739E-2006 history
2006SAE AMS5739E-2006 Steel@ Corrosion and Moderate Heat Resistant@ Bars@ Forgings@ and Rings 14.5Cr - 6.5Ni - 0.72Ti Solution Heat Treated and Maraged@ 180@000 psi (1240 MPa) Tensile Strength (UNS S36200)
2000SAE AMS5739D-2000 Steel, Corrosion and Moderate Heat Resistant, Bars, Forgings, and Rings 14.5Cr - 6.5Ni - 0.72Ti Solution Heat Treated and Maraged, 180,000 psi (1240 MPa) Tensile Strength
1991SAE AMS5739D-1991 Steel@ Corrosion and Moderate Heat Resistant@ Bars@ Forgings@ and Rings 14.5Cr - 6.5Ni - 0.72Ti Solution Heat Treated and Maraged@ 180@000 psi (1240 MPa) Tensile Strength (Reaf. Noncur. November 2000; UNS S36200)
1987SAE AMS5739D-1987 Steel, Corrosion and Moderate Heat Resistant, Bars, Forgings, and Rings, 14.5Cr 6.5Ni 0.72Ti, Solution Heat Treated and Maraged, 180,000 psi (1240 MPa) Tensile Strength
1987SAE AMS5739C-1987 STEEL BARS, FORGINGS, AND RINGS, CORROSION AND MODERATE HEAT RESISTANT 14.5Cr - 6.5Ni - 0.72Ti Solution Heat Treated and Maraged, 180,000 psi (1240 MPa) Tensile Strength
1981SAE AMS5739B-1981 STEEL BARS, FORGINGS, AND RINGS, CORROSION AND MODERATE HEAT RESISTANT 14.5Cr - 6.5Ni - 0.72Ti Solution Heat Treated and Maraged, 180,000 psi (1241 MPa) Tensile Strength
1974SAE AMS5739A-1974 STEEL BARS, FORGINGS, AND RINGS, CORROSION AND MODERATE HEAT RESISTANT 14.5Cr - 6.5Ni - 0.72Ti Solution Treated and Maraged, 180,000 psi (1241 MPa) Tensile Strength
1968SAE AMS5739-1968 STEEL BARS, FORGINGS, AND RINGS, CORROSION AND MODERATE HEAT RESISTANT 14.5Cr - 6.5Ni - 0.72Ti Solution Treated and Maraged (180,000 psi)