ASTM F2660-20 Standard Test Method for Qualifying Coatings for Use on F3125 Grade A490 Structural Bolts Relative to Environmental Hydrogen Embrittlement
1.1 This test method defines the procedures and tests to evaluate the effect of a coating system on the susceptibility to environmental hydrogen embrittlement (EHE) of an ASTM F3125 Grade A490 high strength structural bolt.
1.2 This test method shall qualify a coating system for use with any size of F3125 Grade A490 bolts (that is, 1⁄2 to 1-1⁄2 in.) high strength structural bolts, relative to EHE.
1.3 The characteristic to be evaluated by this test method is the susceptibility to EHE caused by hydrogen generated from corrosion protection of the steel bolt by sacrificial galvanic corrosion of the coating. Testing shall be performed on coated, specimen ASTM F3125 Grade A490 bolts manufactured to the maximum susceptible tensile strength values (see Table 1) of the bolt (see Section 5 Specimen Bolt Requirements). The internal hydrogen embrittlement (IHE) susceptibility will also be inherently evaluated when the EHE is tested through this test method. There is no need for a separate IHE susceptibility test.
1.4 The values stated in inch-pound units are to be regarded as standard. No other units of measurement are included in this standard.
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
ASTM F2660-20 Referenced Document
ASTM E4 Standard Practices for Force Verification of Testing Machines
ASTM E8/E8M Standard Test Methods for Tension Testing of Metallic Materials*, 2024-01-01 Update
ASTM F1624 Standard Test Method for Measurement of Hydrogen Embrittlement Threshold in Steel by the Incremental Step Loading Technique
ASTM F1789 Standard Terminology for F16 Mechanical Fasteners*, 2023-11-01 Update
ASTM F2078 Standard Terminology Relating to Hydrogen Embrittlement Testing*, 2022-05-01 Update
ASTM F3125 Standard Specification for High Strength Structural Bolts, Steel and Alloy Steel, Heat Treated, 120 ksi (830 MPa) and 150 ksi (1040 MPa) Minimum Tensile Strength, Inch and Metric Dimensions*, 2024-04-22 Update
ASTM F519 Standard Test Method for Mechanical Hydrogen Embrittlement Evaluation of Plating Processes and Service Environments
ASTM F606/F606M Standard Test Methods for Determining the Mechanical Properties of Externally and Internally Threaded Fasteners, Washers, Direct Tension Indicators, and Rivets*, 2021-06-01 Update
ASTM G15 Standard Terminology Relating to Corrosion and Corrosion Testing
ASTM G3 Standard Practice for Conventions Applicable to Electrochemical Measurements in Corrosion Testing
ASTM G44 Standard Practice for Exposure of Metals and Alloys by Alternate Immersion in Neutral 3.5?% Sodium Chloride Solution
ASTM G82 Standard Guide for Development and Use of a Galvanic Series for Predicting Galvanic Corrosion Performance*, 2024-04-22 Update
ISO/IEC 17025 General requirements for the competence of testing and calibration laboratories [Standard in French]
ASTM F2660-20 history
2020ASTM F2660-20 Standard Test Method for Qualifying Coatings for Use on F3125 Grade A490 Structural Bolts Relative to Environmental Hydrogen Embrittlement
2013ASTM F2660-13 Standard Test Method for Qualifying Coatings for Use on A490 Structural Bolts Relative to Environmental Hydrogen Embrittlement
2012ASTM F2660-12 Standard Test Method for Qualifying Coatings for Use on A490 Structural Bolts Relative to Hydrogen Embrittlement