1.1 This practice covers the determination of the timetemperature effect of overbaking on the physical and chemical properties of organic coatings.
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of whoever uses this standard to consult and establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. Specific hazard statements are given in Section 7.
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
ASTM D2454-18 Referenced Document
ASTM D1005 Standard Test Method for Measurement of Dry-Film Thickness of Organic Coatings Using Micrometers*, 2020-06-01 Update
ASTM D1308 Standard Test Method for Effect of Household Chemicals on Clear and Pigmented Organic Finishes
ASTM D1640 Standard Test Methods for Drying, Curing, or Film Formation of Organic Coatings at Room Temperature
ASTM D1729 Standard Practice for Visual Appraisal of Colors and Color Differences of Diffusely-Illuminated Opaque Materials
ASTM D1730 Standard Practices for Preparation of Aluminum and Aluminum-Alloy Surfaces for Painting
ASTM D1731 Standard Practices for Preparation of Hot-Dip Aluminum Surfaces for Painting
ASTM D2197 Standard Test Method for Adhesion of Organic Coatings by Scrape Adhesion
ASTM D2201 Standard Practice for Preparation of Zinc-Coated and Zinc-Alloy-Coated Steel Panels for Testing Paint and Related Coating Products
ASTM D2244 Standard Test Method for Calculation of Color Differences From Instrumentally Measured Color Coordinates
ASTM D2794 Standard Test Method for Resistance of Organic Coatings to the Effects of Rapid Deformation (Impact)*, 2024-01-25 Update
ASTM D3359 Standard Test Methods for Measuring Adhesion by Tape Test
ASTM D3363 Standard Test Method for Film Hardness by Pencil Test*, 2022-06-01 Update
ASTM D522 Standard Test Methods for Mandrel Bend Test of Attached Organic Coatings
ASTM D609 Standard Practice for Preparation of Cold-Rolled Steel Panels for Testing Paint, Varnish, Conversion Coatings, and Related Coating Products*, 2022-06-01 Update
ASTM D6386 Standard Practice for Preparation of Zinc (Hot-Dip Galvanized) Coated Iron and Steel Product and Hardware Surfaces for Painting
ASTM D7091 Standard Practice for Nondestructive Measurement of Dry Film Thickness of Nonmagnetic Coatings Applied to Ferrous Metals and Nonmagnetic, Nonconductive Coatings Applied to Non-Ferrous Metals*, 2022-06-01 Update
ASTM D7396 Standard Guide for Preparation of New, Continuous Zinc-Coated (Galvanized) Steel Surfaces for Painting*, 2024-04-22 Update
ASTM D823 Standard Practices for Producing Films of Uniform Thickness of Paint, Varnish, and Related Products on Test Panels
ASTM E805 Standard Practice for Identification of Instrumental Methods of Color or Color-Difference Measurement of Materials
ASTM D2454-18 history
2023ASTM D2454-23 Standard Practice for Determining the Effect of Overbaking on Organic Coatings
2018ASTM D2454-18 Standard Practice for Determining the Effect of Overbaking on Organic Coatings
2014ASTM D2454-14 Standard Practice for Determining the Effect of Overbaking on Organic Coatings
2008ASTM D2454-08 Standard Practice for Determining the Effect of Overbaking on Organic Coatings
1995ASTM D2454-95(2002) Standard Practice for Determining the Effect of Overbaking on Organic Coatings
1995ASTM D2454-95 Standard Practice for Determining the Effect of Overbaking on Organic Coatings