ASTM D6386-99(2005)
Standard Practice for Preparation of Zinc (Hot-Dip Galvanized) Coated Iron and Steel Product and Hardware Surfaces for Painting
- Standard No.
- ASTM D6386-99(2005)
- Release Date
- 1999
- Published By
- American Society for Testing and Materials (ASTM)
- Status
- Replace By
- ASTM D6386-10
- Latest
- ASTM D6386-22
- Scope
This practice describes the procedures that can be used to prepare new and weathered zinc-coated surfaces on after-fabrication steel products for painting, and that can improve the bond of paint to the zinc surface.
1.1 This practice describes methods of preparing surfaces of new and weathered hot-dip galvanized steel for painting. Hot-dip galvanized steel is produced by the immersion of fabricated or unfabricated products in a bath of molten zinc, as specified in Specifications A 123 or A153/A153M. This practice covers surface preparation on iron and steel products and hardware that have not been painted previously. Galvanized surfaces may have been treated with protective coatings to prevent the occurrence of wet storage stain. This practice does not apply to sheet galvanized steel products nor to the coil coating or continuous roller coating processes.
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
ASTM D6386-99(2005) Referenced Document
- ASTM A123 Standard specifications for zinc (hot-dip galvanizing) coatings on iron and steel products*， 2024-04-19 Update
- ASTM A780 Standard Practice for Repair of Damaged and Uncoated Areas of Hot-Dip Galvanized Coatings*， 2024-04-19 Update
- ASTM B201 Standard Practice for Testing Chromate Coatings on Zinc and Cadmium Surfaces*， 2019-04-01 Update
- ASTM E376 Standard Practice for Measuring Coating Thickness by Magnetic-Field or Eddy-Current (Electromagnetic) Test Methods
ASTM D6386-99(2005) history
- 2022 ASTM D6386-22 Standard Practice for Preparation of Zinc (Hot-Dip Galvanized) Coated Iron and Steel Product and Hardware Surfaces for Painting
- 2016 ASTM D6386-16a Standard Practice for Preparation of Zinc (Hot-Dip Galvanized) Coated Iron and Steel Product and Hardware Surfaces for Painting
- 2016 ASTM D6386-16 Standard Practice for Preparation of Zinc (Hot-Dip Galvanized) Coated Iron and Steel Product and Hardware Surfaces for Painting
- 2010 ASTM D6386-10 Standard Practice for Preparation of Zinc (Hot-Dip Galvanized) Coated Iron and Steel Product and Hardware Surfaces for Painting
- 1999 ASTM D6386-99(2005) Standard Practice for Preparation of Zinc (Hot-Dip Galvanized) Coated Iron and Steel Product and Hardware Surfaces for Painting
- 1999 ASTM D6386-99 Standard Practice for Preparation of Zinc (Hot-Dip Galvanized) Coated Iron and Steel Product and Hardware Surfaces for Painting