1.1 This test method permits the estimation of the relative ability of rubber compounds used for applications requiring resistance to outdoor weathering.
1.2 This test method is not applicable to materials ordinarily classed as hard rubber, but is adaptable to molded or extruded soft rubber materials and sponge rubber for use in window weatherstripping as well as similar automotive applications.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
ASTM D1171-18 Referenced Document
ASTM D1149 Standard Test Method for Rubber Deterioration-Surface Ozone Cracking in a Chamber
ASTM D518 Standard Test Method for Rubber Deterioration-Surface Cracking
ASTM D1171-18 history
2018ASTM D1171-18 Standard Test Method for Rubber Deterioration—Surface Ozone Cracking Outdoors (Triangular Specimens)
2016ASTM D1171-16e1 Standard Test Method for Rubber Deterioration—Surface Ozone Cracking Outdoors (Triangular Specimens)
2016ASTM D1171-16 Standard Test Method for Rubber Deterioration&x2014;Surface Ozone Cracking Outdoors (Triangular Specimens)
2015ASTM D1171-15 Standard Test Method for Rubber Deterioration&x2014;Surface Ozone Cracking Outdoors or Chamber (Triangular Specimens)
1999ASTM D1171-99(2007) Standard Test Method for Rubber Deteriorationx2014;Surface Ozone Cracking Outdoors or Chamber (Triangular Specimens)
1999ASTM D1171-99 Standard Test Method for Rubber Deterioration-Surface Ozone Cracking Outdoors or Chamber (Triangular Specimens)