ASTM D1149-99
Standard Test Method for Rubber Deterioration-Surface Ozone Cracking in a Chamber

Standard No.

ASTM D1149-99

Release Date

1999

Published By

American Society for Testing and Materials (ASTM)

Status

Be replaced

Replace By

ASTM D1149-07

Latest

ASTM D1149-18

Scope

1.1 This test method covers the estimation of the resistance of vulcanized rubber to cracking when exposed to an atmosphere containing ozone. The rubber specimens are kept under a surface tensile strain, and the ozone content or partial pressure in the test chamber is maintained at a fixed value.

1.2 The values stated in SI units are to be regarded as the standard. The values in parentheses are for information only.

1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. For a specific hazard statement, see Note 1 and 7.1.

Note 1-Ozone is a hazardous chemical.

ASTM D1149-99 history

• 2018 ASTM D1149-18 Standard Test Methods for Rubber Deterioration&x2014;Cracking in an Ozone Controlled Environment
• 2016 ASTM D1149-16 Standard Test Methods for Rubber Deterioration&x2014;Cracking in an Ozone Controlled Environment
• 2015 ASTM D1149-15 Standard Test Methods for Rubber Deterioration&x2014;Cracking in an Ozone Controlled Environment
• 2007 ASTM D1149-07(2012) Standard Test Methods for Rubber Deteriorationmdash;Cracking in an Ozone Controlled Environment
• 2007 ASTM D1149-07 Standard Test Methods for Rubber Deterioration-Cracking in an Ozone Controlled Environment
• 1999 ASTM D1149-99 Standard Test Method for Rubber Deterioration-Surface Ozone Cracking in a Chamber
• 1978 ASTM D1149-78a Standard Test Method for Rubber Deterioration - Surface Ozone Cracking In A Chamber ( Flat Specimen)