SAE AMS5356D-2016
Steel@ Corrosion Resistant@ Investment Castings 15Cr - 4.6Ni - 0.22Cb - 2.8Cu Solution and Precipitation Heat Treated (H1100) 130 ksi (896 MPa) Tensile Strength (UNS J92110)
- Standard No.
- SAE AMS5356D-2016
- Release Date
- 2016
- Published By
- SAE - SAE International
- Status
- Replace By
- SAE AMS5356D-2022
- Latest
- SAE AMS5356D-2022
- Scope
- Form This specification covers a corrosion resistant steel in the form of investment castings. Application These castings have been used typically for parts requiring good corrosion resistance and strength up to 600 ??(316 ??@ but usage is not limited to such applications (see 8.3).
SAE AMS5356D-2016 history
- 2022 SAE AMS5356D-2022 Steel, Corrosion-Resistant, Investment Castings 15Cr - 4.6Ni - 0.22Cb - 2.8Cu Solution and Precipitation Heat Treated (H1100) 130 ksi (896 MPa) Tensile Strength
- 2016 SAE AMS5356D-2016 Steel@ Corrosion Resistant@ Investment Castings 15Cr - 4.6Ni - 0.22Cb - 2.8Cu Solution and Precipitation Heat Treated (H1100) 130 ksi (896 MPa) Tensile Strength (UNS J92110)
- 2011 SAE AMS5356-2011 STEEL CASTINGS, INVESTMENT, CORROSION RESISTANT 15Cr - 4.6Ni - 0.22(Cb + Ta) - 2.8Cu Solution and Precipitation Heat Treated 130,000 psi (696 MPa) Tensile Strength
- 2010 SAE AMS5356C-2010 Steel, Corrosion Resistant, Investment Castings 15Cr 4.6Ni 0.22Cb 2.8Cu Solution and Precipitation Heat Treated (H1100) 130 ksi (896 MPa) Tensile Strength
- 2006 SAE AMS5356B-2006 Steel, Corrosion Resistant, Investment Castings 15Cr - 4.6Ni - 0.22Cb - 2.8Cu Solution and Precipitation Heat Treated (H1100) 130 ksi (896 MPa) Tensile Strength
- 2001 SAE AMS5356B-2001 Steel, Corrosion Resistant, Investment Castings 15Cr 4.6Ni 0.22Cb 2.8Cu Solution and Precipitation Heat Treated (H1100) 130 ksi (896 MPa) Tensile Strength
- 1995 SAE AMS5356A-1995 Steel, Corrosion Resistant, Investment Castings 15Cr 4.6Ni 0.22Cb 2.8Cu Solution and Precipitation Heat Treated (H1100) 130 ksi (896 MPa) Tensile Strength