SAE AMS4776E-1994
Nickel Alloy@ Brazing Filler Metal 73Ni - 4.5Si - 14Cr - 3.1B - 4.5Fe (Low Carbon) 1790 to 1970 °F (977 to 1077 °C) Solidus-Liquidus Range (UNS N99610)

Standard No.

SAE AMS4776E-1994

Release Date

1994

Published By

SAE - SAE International

Status

Be replaced

Replace By

SAE AMS4776F-1995

Latest

SAE AMS4776K-2023

Scope

Form: This specification covers a nickel alloy in the form of wire@ rod@ strip@ foil@ and powder and a viscous mixture (paste) of the powder in a suitable binder. Application: This filler metal has been used typically for joining corrosion and heat resistant steels and alloys requiring corrosion and oxidation resistant joints with good strength at elevated temperatures are required. Also may be used as a corrosion and oxidation resistant hard coating.

SAE AMS4776E-1994 history

• 2023 SAE AMS4776K-2023 Nickel Alloy, Brazing Filler Metal, 73Ni - 4.5Si - 14Cr - 3.1B - 4.5Fe (Low Carbon), 1790 °F (977 °C) Solidus to 1970 °F (1077 °C) Liquidus Range
• 2018 SAE AMS4776J-2018 Nickel Alloy@ Brazing Filler Metal 73Ni - 4.5Si - 14Cr - 3.1B - 4.5Fe (Low Carbon) 1790 °F (977 °C) Solidus to 1970 °F (1077 °C) Liquidus Range (UNS N99610)
• 2010 SAE AMS4776H-2010 Nickel Alloy, Brazing Filler Metal 73Ni - 4.5Si - 14Cr - 3.1B - 4.5Fe (Low Carbon) 1790 to 1970 °F (977 to 1077 °C) Solidus-Liquidus Range (UNS N99610)
• 2005 SAE AMS4776G-2005 Nickel Alloy, Brazing Filler Metal 73Ni 4.5Si 14Cr 3.1B 4.5Fe (Low Carbon) 1790 to 1970°F (977 to 1077°C) Solidus-Liquidus Range
• 2000 SAE AMS4776F-2000 Nickel Alloy, Brazing Filler Metal 73Ni - 4.5Si - 14Cr - 3.1B - 4.5Fe (Low Carbon) 1790 to 1970 °F (977 to 1077 °C) Solidus-Liquidus Range
• 1995 SAE AMS4776F-1995 Nickel Alloy, Brazing Filler Metal 73Ni 4.5Si 14Cr 3.1B 4.5Fe (Low Carbon) 1790 to 1970°F (977 to 1077°C) Solidus-Liquidus Range (Reaffirmed: 01 Aug 2000)
• 1994 SAE AMS4776E-1994 Nickel Alloy@ Brazing Filler Metal 73Ni - 4.5Si - 14Cr - 3.1B - 4.5Fe (Low Carbon) 1790 to 1970 °F (977 to 1077 °C) Solidus-Liquidus Range (UNS N99610)
• 1992 SAE AMS4776D-1992 Nickel Alloy@ Brazing Filler Metal 73Ni - 4.5Si - 14Cr - 3.1B - 4.5Fe (Low Carbon) 1790 to 1970 °F (977 to 1077 °C) Solidus-Liquidus Range (UNS N99610)
• 1988 SAE AMS4776C-1988 Brazing Filler Metal@ Nickel Alloy 73Ni - 4.5Si - 14Cr - 3.1B - 4.5Fe (Low Carbon) 1790 to 1970 °F (977 to 1077 °C) Solidus-Liquidus Range (UNS N99610)
• 1981 SAE AMS4776B-1981 Brazing Filler Metal@ Nickel 73Ni - 4.5Si - 14Cr - 3.1B - 4.5Fe (Low Carbon) 1790° - 1970°F (975° - 1075°C) Solidus-Liquidus Range
• 1978 SAE AMS4776A-1978 Brazing Filler Metal@ Nickel 73Ni - 4.5Si - 14Cr - 3.1B - 4.5Fe (Low Carbon) 1790° - 1970°F (975° - 1075°C) Solidus-Liquidus Range
• 1956 SAE AMS4776-1956 Brazing Alloy Nickel Base - 4Si - 16.5Cr - 4Fe - 3.8B - Low Carbon