SAE AMS4776-1956
Brazing Alloy Nickel Base - 4Si - 16.5Cr - 4Fe - 3.8B - Low Carbon
Home
SAE AMS4776-1956
Standard No.
SAE AMS4776-1956
Release Date
1956
Published By
SAE - SAE International
Status
Be replaced
2012-12
Replace By
SAE AMS4776A-1978
Latest
SAE AMS4776K-2023
Scope
APPLICATION: Primarily for joining corrosion and heat resistant alloys where corrosion and oxidation resistant joints with good strength at high temperatures are required. Also used as a corrosion and oxidation resistant hard coating.
SAE AMS4776-1956 history
2023
SAE AMS4776K-2023
Nickel Alloy, Brazing Filler Metal, 73Ni - 4.5Si - 14Cr - 3.1B - 4.5Fe (Low Carbon), 1790 °F (977 °C) Solidus to 1970 °F (1077 °C) Liquidus Range
2018
SAE AMS4776J-2018
Nickel Alloy@ Brazing Filler Metal 73Ni - 4.5Si - 14Cr - 3.1B - 4.5Fe (Low Carbon) 1790 °F (977 °C) Solidus to 1970 °F (1077 °C) Liquidus Range (UNS N99610)
2010
SAE AMS4776H-2010
Nickel Alloy, Brazing Filler Metal 73Ni - 4.5Si - 14Cr - 3.1B - 4.5Fe (Low Carbon) 1790 to 1970 °F (977 to 1077 °C) Solidus-Liquidus Range (UNS N99610)
2005
SAE AMS4776G-2005
Nickel Alloy, Brazing Filler Metal 73Ni 4.5Si 14Cr 3.1B 4.5Fe (Low Carbon) 1790 to 1970°F (977 to 1077°C) Solidus-Liquidus Range
2000
SAE AMS4776F-2000
Nickel Alloy, Brazing Filler Metal 73Ni - 4.5Si - 14Cr - 3.1B - 4.5Fe (Low Carbon) 1790 to 1970 °F (977 to 1077 °C) Solidus-Liquidus Range
1995
SAE AMS4776F-1995
Nickel Alloy, Brazing Filler Metal 73Ni 4.5Si 14Cr 3.1B 4.5Fe (Low Carbon) 1790 to 1970°F (977 to 1077°C) Solidus-Liquidus Range (Reaffirmed: 01 Aug 2000)
1994
SAE AMS4776E-1994
Nickel Alloy@ Brazing Filler Metal 73Ni - 4.5Si - 14Cr - 3.1B - 4.5Fe (Low Carbon) 1790 to 1970 °F (977 to 1077 °C) Solidus-Liquidus Range (UNS N99610)
1992
SAE AMS4776D-1992
Nickel Alloy@ Brazing Filler Metal 73Ni - 4.5Si - 14Cr - 3.1B - 4.5Fe (Low Carbon) 1790 to 1970 °F (977 to 1077 °C) Solidus-Liquidus Range (UNS N99610)
1988
SAE AMS4776C-1988
Brazing Filler Metal@ Nickel Alloy 73Ni - 4.5Si - 14Cr - 3.1B - 4.5Fe (Low Carbon) 1790 to 1970 °F (977 to 1077 °C) Solidus-Liquidus Range (UNS N99610)
1981
SAE AMS4776B-1981
Brazing Filler Metal@ Nickel 73Ni - 4.5Si - 14Cr - 3.1B - 4.5Fe (Low Carbon) 1790° - 1970°F (975° - 1075°C) Solidus-Liquidus Range
1978
SAE AMS4776A-1978
Brazing Filler Metal@ Nickel 73Ni - 4.5Si - 14Cr - 3.1B - 4.5Fe (Low Carbon) 1790° - 1970°F (975° - 1075°C) Solidus-Liquidus Range
1956
SAE AMS4776-1956
Brazing Alloy Nickel Base - 4Si - 16.5Cr - 4Fe - 3.8B - Low Carbon
Copyright ©2024 All Rights Reserved