SAE AMS5853D-2019
Steel@ Corrosion and Heat-Resistant@ Bars and Wire 15Cr - 25.5Ni - 1.2Mo - 2.1Ti - 0.006B - 0.30V Consumable Electrode Melted 1800 °F (982 °C) Solution Treated and Work-Strengthened 160 ksi (1103 MPa) Tensile Strength (UNS S66286)

Standard No.

SAE AMS5853D-2019

Release Date

2019

Published By

SAE - SAE International

Status

Be replaced

Replace By

SAE AMS5853E-2024

Latest

SAE AMS5853E-2024

Scope

Form This specification covers a corrosion and heat-resistant steel in the form of work-strengthened bars and wire@ 1-1/4 inches (31.8 mm) and under in nominal diameter or least distance between parallel sides (see 8.6). Application These products have been used typically for parts@ such as fasteners@ requiring room-temperature minimum tensile strength of 160 ksi (1103 MPa) after precipitation heat treatment@ for use up to 1000 ??(538 ?? and having oxidation resistance up to 1200 ??(649 ??@ but usage is not limited to such applications.

SAE AMS5853D-2019 history

• 2024 SAE AMS5853E-2024 Steel, Corrosion- and Heat-Resistant, Bars and Wire 15Cr - 25.5Ni - 1.2Mo - 2.1Ti - 0.006B - 0.30V Consumable Electrode Remelted 1800 °F (982 °C) Solution Heat Treated and Work-Strengthened 160 ksi (1103 MPa) Tensile Strength Capability
• 2019 SAE AMS5853D-2019 Steel@ Corrosion and Heat-Resistant@ Bars and Wire 15Cr - 25.5Ni - 1.2Mo - 2.1Ti - 0.006B - 0.30V Consumable Electrode Melted 1800 °F (982 °C) Solution Treated and Work-Strengthened 160 ksi (1103 MPa) Tensile Strength (UNS S66286)
• 2012 SAE AMS5853C-2012 Steel, Corrosion and Heat-Resistant, Bars and Wire 15Cr - 25.5Ni - 1.2Mo - 2.1Ti - 0.006B - 0.30V Consumable Electrode Melted 1800 °F (982 °C) Solution Treated and Work-Strengthened 160 ksi (1103 MPa) Tensile Strength
• 2006 SAE AMS5853C-2006 Steel, Corrosion and Heat Resistant, Bars and Wire 15Cr - 25.5Ni - 1.2Mo - 2.1Ti - 0.006B - 0.30V Consumable Electrode Melted 1800 Degrees F (982 Degrees C) Solution Treated and Work-Strengthened 160 ksi (1103 MPa) Tensile Strength UNS S66286
• 2000 SAE AMS5853B-2000 Steel, Corrosion and Heat Resistant, Bars and Wire 15Cr 25.5Ni 1.2Mo 2.1Ti 0.006B 0.30V, Consumable Electrode Melted 1800°F (982°C) Solution Treated and Work-Strengthened 160 ksi (1103 MPa) Tensile Strength
• 1993 SAE AMS5853A-1993 Steel@ Corrosion and Heat Resistant@ Bars and Wire 15Cr - 25.5Ni - 1.2Mo - 2.1Ti - 0.006B - 0.30V Consumable Electrode Melted 1800 Degrees F (982 Degrees C) Solution Treated and Work-Strengthened 160 ksi (1103 MPa) Tensile Strength (UNS K66286)
• 1991 SAE AMS5853-1991 STEEL BARS, CORROSION AND HEAT RESISTANT 15Cr - 25.5Ni - 1.2Mo - 2.1Ti - 0.006B - 0.30V 1800°F (980°C) Solution Treated and Work-Strengthened 160,000 psi (1105 MPa) Tensile Strength, Consumable Electrode Melted