ASTM C1582/C1582M-11(2017)e1
Standard Specification for Admixtures to Inhibit Chloride-Induced Corrosion of Reinforcing Steel in Concrete

Standard No.

ASTM C1582/C1582M-11(2017)e1

Release Date

2017

Published By

American Society for Testing and Materials (ASTM)

Latest

ASTM C1582/C1582M-11(2017)e1

Scope

1.1 This specification covers material for use as chloridecorrosion-inhibiting admixtures for concrete. 1.2 Results of the tests conducted to meet this specification are not to be used to rank the expected field performance of various chloride-corrosion-inhibiting admixtures. 1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard. 1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory requirements prior to use. (Warning— Fresh hydraulic cementitious mixtures are caustic and may cause chemical burns to skin and tissue upon prolonged exposure.2 ) 1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ASTM C1582/C1582M-11(2017)e1 Referenced Document

• ASTM C1152/C1152M Standard Test Method for Acid-Soluble Chloride in Mortar and Concrete
• ASTM C125 Standard Terminology Relating to Concrete and Concrete Aggregates*， 2021-10-01 Update
• ASTM C143/C143M Standard Test Method for Slump of Hydraulic-Cement Concrete*， 2020-06-01 Update
• ASTM C150/C150M Standard Specification for Portland Cement*， 2022-07-01 Update
• ASTM C157/C157M Standard Test Method for Length Change of Hardened Hydraulic-Cement, Mortar, and Concrete
• ASTM C231/C231M Standard Test Method for Air Content of Freshly Mixed Concrete by the Pressure Method*， 2024-01-01 Update
• ASTM C260/C260M Standard Specification for Air-Entraining Admixtures for Concrete*， 2024-04-21 Update
• ASTM C39/C39M Standard Test Method for Compressive Strength of Cylindrical Concrete Specimens
• ASTM C403/C403M Standard Test Method for Time of Setting of Concrete Mixtures by Penetration Resistance
• ASTM C494/C494M Standard Specification for Chemical Admixtures for Concrete
• ASTM C666/C666M Standard Test Method for Resistance of Concrete to Rapid Freezing and Thawing*， 2024-04-21 Update
• ASTM C78/C78M Standard Test Method for Flexural Strength of Concrete (Using Simple Beam with Third-Point Loading)*， 2022-03-01 Update
• ASTM G109 Standard Test Method for Determining the Effects of Chemical Admixtures on the Corrosion of Embedded Steel Reinforcement in Concrete Exposed to Chloride Environments
• ASTM G15 Standard Terminology Relating to Corrosion and Corrosion Testing
• ASTM G180 Standard Test Method for Corrosion Inhibiting Admixtures for Steel in Concrete by Polarization Resistance in Cementitious Slurries*， 2023-06-01 Update

ASTM C1582/C1582M-11(2017)e1 history

• 2017 ASTM C1582/C1582M-11(2017)e1 Standard Specification for Admixtures to Inhibit Chloride-Induced Corrosion of Reinforcing Steel in Concrete
• 2011 ASTM C1582/C1582M-11 Standard Specification for Admixtures to Inhibit Chloride-Induced Corrosion of Reinforcing Steel in Concrete
• 2004 ASTM C1582/C1582M-04 Standard Specification for Admixtures to Inhibit Chloride-Induced Corrosion of Reinforcing Steel in Concrete