ASTM C150/C150M-22
Standard Specification for Portland Cement

Standard No.
ASTM C150/C150M-22
Release Date
2022
Published By
American Society for Testing and Materials (ASTM)
Latest
ASTM C150/C150M-22
Scope
1.1 This specification covers ten types of portland cement, as follows (see Note 2): 1.1.1 Type I—For general use, when the special properties specified for any other type are not required. 1.1.2 Type IA—Air-entraining cement for the same uses as Type I, where air-entrainment is desired. 1.1.3 Type II—For general use, more especially when moderate sulfate resistance is desired. 1.1.4 Type IIA—Air-entraining cement for the same uses as Type II, where air-entrainment is desired. 1.1.5 Type II(MH)—For general use, more especially when moderate heat of hydration and moderate sulfate resistance are desired. 1.1.6 Type II(MH)A—Air-entraining cement for the same uses as Type II(MH), where air-entrainment is desired. 1.1.7 Type III—For use when high early strength is desired. 1.1.8 Type IIIA—Air-entraining cement for the same use as Type III, where air-entrainment is desired. 1.1.9 Type IV—For use when a low heat of hydration is desired. 1.1.10 Type V—For use when high sulfate resistance is desired. NOTE 1—Some cements are designated with a combined type classification, such as Type I/II, indicating that the cement meets the requirements of the indicated types and is being offered as suitable for use when either type is desired. NOTE 2—Cement conforming to the requirements for all types are not carried in stock in some areas. In advance of specifying the use of cement other than Type I, determine whether the proposed type of cement is or can be made available. 1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard. Values in SI units [or inch-pound units] shall be obtained by measurement in SI units [or inch-pound units] or by appropriate conversion, using the Rules for Conversion and Rounding given in IEEE/ASTM SI 10, of measurements made in other units [or SI units]. Values are stated in only SI units when inch-pound units are not used in practice. 1.3 The text of this specification references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard. 1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ASTM C150/C150M-22 Referenced Document

  • ASTM C1038/C1038M Standard Test Method for Expansion of Hydraulic Cementitious Material Mortar Bars Stored in Water*， 2024-04-01 Update
  • ASTM C109/C109M Standard Test Method for Compressive Strength of Hydraulic Cement Mortars (Using 2-in. or [50-mm] Cube Specimens)
  • ASTM C114 Standard Test Methods for Chemical Analysis of Hydraulic Cement*， 2023-10-01 Update
  • ASTM C1702 Standard Test Method for Measurement of Heat of Hydration of Hydraulic Cementitious Materials Using Isothermal Conduction Calorimetry*， 2023-08-01 Update
  • ASTM C1778 Standard Guide for Reducing the Risk of Deleterious Alkali-Aggregate Reaction in Concrete*， 2023-12-01 Update
  • ASTM C183/C183M Standard Practice for Sampling and the Amount of Testing of Hydraulic Cement*， 2023-06-01 Update
  • ASTM C185 Standard Test Method for Air Content of Hydraulic Cement Mortar
  • ASTM C191 Standard Test Method for Time of Setting of Hydraulic Cement by Vicat Needle
  • ASTM C204 Standard Test Methods for Fineness of Hydraulic Cement by Air-Permeability Apparatus
  • ASTM C219 Standard Terminology Relating to Hydraulic and Other Inorganic Cements*， 2024-04-01 Update
  • ASTM C226 Standard Specification for Air-Entraining Additions for Use in the Manufacture of Air-Entraining Hydraulic Cement
  • ASTM C266 Standard Test Method for Time of Setting of Hydraulic-Cement Paste by Gillmore Needles
  • ASTM C451 Standard Test Method for Early Stiffening of Hydraulic Cement (Paste Method)
  • ASTM C452 Standard Test Method for Potential Expansion of Portland-Cement Mortars Exposed to Sulfate
  • ASTM C465 Standard Specification for Processing Additions for Use in the Manufacture of Hydraulic Cements
  • ASTM C51 Standard Terminology Relating to Lime and Limestone (as Used by the Industry)*， 2023-10-01 Update
  • ASTM C563 Standard Test Method for Optimum SO3 in Hydraulic Cement Using 24-h Compressive Strength
  • ASTM E29 Standard Practice for Using Significant Digits in Test Data to Determine Conformance with Specifications
  • IEEE/ASTM SI 10 American National Standard for Metric Practice

ASTM C150/C150M-22 history

Standard Specification for Portland Cement


Copyright ©2024 All Rights Reserved