ASTM D2370-16(2021) PDF

Scope: 1.1 This test method covers the determination of the elongation, tensile strength, and stiffness (modulus of elasticity) of organic coatings when tested as free films. 1.2 The values stated in SI units are to be regarded as standard. The values given in parentheses are mathematical conversions to inch-pound units that are provided for information only and are not considered standard. 1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. 1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ASTM D2370-16(2021) Referenced Document

ASTM D1005 Standard Test Method for Measurement of Dry-Film Thickness of Organic Coatings Using Micrometers
ASTM D3980 Standard Practice for Interlaboratory Testing of Paint and Related Materials
ASTM D4708 Standard Practice for Preparation of Uniform Free Films of Organic Coatings
ASTM D823 Standard Practices for Producing Films of Uniform Thickness of Paint, Varnish, and Related Products on Test Panels
ASTM D882 Standard Test Method for Tensile Properties of Thin Plastic Sheeting

2021 ASTM D2370-16(2021) Standard Test Method for Tensile Properties of Organic Coatings
2016 ASTM D2370-16 Standard Test Method for Tensile Properties of Organic Coatings
1998 ASTM D2370-98(2010) Standard Test Method for Tensile Properties of Organic Coatings
1998 ASTM D2370-98(2002)e1 Standard Test Method for Tensile Properties of Organic Coatings
1998 ASTM D2370-98(2002) Standard Test Method for Tensile Properties of Organic Coatings
1998 ASTM D2370-98 Standard Test Method for Tensile Properties of Organic Coatings