ASTM C607-88(2016) PDF

Scope: 3.1 This practice is useful for preparing coked specimens for subsequent testing where the shapes desired cannot be fitted into the coking box described in Test Methods C831.

3.2 This practice can be very sensitive to heating rates in coking. Thus, strict adherence to the coking procedure is necessary.

1.1 This practice covers the preparation of coking of carbon-bearing material for subsequent testing such as modulus of rupture, slag testing, thermal conductivity, and thermal expansion. Test Methods C831 is the specified method for testing residual carbon.

1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ASTM C607-88(2016) Referenced Document

ASTM C133 Standard Test Methods for Cold Crushing Strength and Modulus of Rupture of Refractories*， 2024-04-20 Update
ASTM C767 Standard Test Method for Thermal Conductivity of Carbon Refractories*， 1993-04-20 Update
ASTM C831 Standard Test Methods for Residual Carbon, Apparent Residual Carbon, and Apparent Carbon Yield in Coked Carbon-Containing Brick and Shapes&x2009;*， 1998-04-20 Update
ASTM C832 Standard Test Method for Measuring Thermal Expansion and Creep of Refractories Under Load*， 2021-08-01 Update
ASTM C874 Standard Practice for Rotary Slag Testing of Refractory Materials*， 1999-04-20 Update

1988 ASTM C607-88(2016) Standard Practice for Coking Large Shapes of Carbon-Bearing Materials
1988 ASTM C607-88(2010)e1 Standard Practice for Coking Large Shapes of Carbon-Bearing Materials
1988 ASTM C607-88(2005) Standard Practice for Coking Large Shapes of Carbon-Bearing Materials
1988 ASTM C607-88(2000) Standard Practice for Coking Large Shapes of Carbon-Bearing Materials