SAE AMS5400C-2014
Steel, Corrosion-Resistant, Investment Castings, 15Cr - 4.6Ni - 0.22Cb - 2.8Cu, Solution and Precipitation Heat Treated (H935), 170 ksi (1172 MPa) Tensile Strength
Home
SAE AMS5400C-2014
Standard No.
SAE AMS5400C-2014
Release Date
2014
Published By
Society of Automotive Engineers (SAE)
Status
Be replaced
Replace By
SAE AMS5400D-2022
Latest
SAE AMS5400D-2022
Scope
This specification covers a corrosion-resistant steel in the form of investment castings.
SAE AMS5400C-2014 Referenced Document
ASTM E1417-05
Standard Practice for Liquid Penetrant Testing
*
,
2024-04-20 Update
ASTM E1444-05
Standard Practice for Magnetic Particle Testing
*
,
2024-04-20 Update
ASTM E1742-08
Standard Practice for Radiographic Examination
*
,
2024-04-20 Update
ASTM E18-14
Standard Test Methods for Rockwell Hardness of Metallic Materials
*
,
2024-04-20 Update
ASTM E8-04
Standard Test Methods for Tension Testing of Metallic Materials
*
,
2024-04-20 Update
SAE AMS5400C-2014 history
2022
SAE AMS5400D-2022
Steel, Corrosion-Resistant, Investment Castings 15Cr - 4.6Ni - 0.22Cb - 2.8Cu Solution and Precipitation Heat Treated (H935) 170 ksi (1172 MPa) Tensile Strength
2014
SAE AMS5400C-2014
Steel, Corrosion-Resistant, Investment Castings, 15Cr - 4.6Ni - 0.22Cb - 2.8Cu, Solution and Precipitation Heat Treated (H935), 170 ksi (1172 MPa) Tensile Strength
2011
SAE AMS5400-2011
STEEL CASTINGS, INVESTMENT, CORROSION RESISTANT 15Cr - 4.6Ni - 0.22(Cb + Ta) - 2.8Cu Solution and Precipitation Heat Treated 170,000 psi (1172 MPa) Tensile Strength
2007
SAE AMS5400B-2007
Steel, Corrosion-Resistant, Investment Castings 15Cr - 4.6Ni - 0.22Cb - 2.8Cu Solution and Precipitation Heat Treated (H935) 170 ksi (1172 MPa) Tensile Strength UNS J92110
1995
SAE AMS5400A-1995
Steel, Corrosion Resistant, Investment Castings, 15Cr 4.6Ni 0.22Cb 2.8Cu, Solution and Precipitation Heat Treated (H935) 170 ksi (1172 MPa) Tensile Strength
Copyright ©2024 All Rights Reserved