This specification covers the requirements for electrodeposition of zinc plating. This process has been used typically to provide corrosion resistance to metal parts, but usage is not limited to such applications. Unless otherwise stated on the engineering drawing, high strength steel parts having a hardness of 45 HRC or greater shall not be electroplated to this document.
SAE AMS2402K-2013 Referenced Document
ASTM A262-13 Standard Practices for Detecting Susceptibility to Intergranular Attack in Austenitic Stainless Steels*, 2024-04-20 Update
ASTM A370-12 Standard Test Methods and Definitions for Mechanical Testing of Steel Products*, 2024-04-20 Update
ASTM A632-04 Standard Specification for Seamless and Welded Austenitic Stainless Steel Tubing (Small-Diameter) for General Service*, 2024-04-20 Update
ASTM B117-11 Standard Practice for Operating Salt Spray (Fog) Apparatus*, 2024-04-20 Update
ASTM B253-11 Standard Guide for Preparation of Aluminum Alloys for Electroplating*, 2024-04-20 Update
ASTM B499-09 Standard Test Method for Measurement of Coating Thicknesses by the Magnetic Method: Nonmagnetic Coatings on Magnetic Basis Metals*, 2024-04-20 Update
ASTM B567-98 Standard Test Method for Measurement of Coating Thickness by the Beta Backscatter Method
ASTM B568-98 Standard Test Method for Measurement of Coating Thickness by X-Ray Spectrometry
ASTM E376-11 Standard Practice for Measuring Coating Thickness by Magnetic-Field or Eddy-Current (Electromagnetic) Testing Methods*, 2024-04-20 Update
ASTM F519-12 Standard Test Method for Mechanical Hydrogen Embrittlement Evaluation of Plating/Coating Processes and Service Environments*, 2024-04-20 Update
ASTM F519-13 Standard Test Method for Mechanical Hydrogen Embrittlement Evaluation of Plating/Coating Processes and Service Environments*, 2024-04-20 Update