This Japanese Industrial Standard specifies the steel sheet and strip (hereafter referred to as "sheet and coil")and corrugated sheet manufactured by processing steel sheet into the shape and dimensions specified in JIS G 3316,which are coated so as to be equal thickness on both surfaces by a hot-dip zinc-aluminium-magnesium alloy coating process. The zinc-aluminium-magnesium alloy composition by mass fraction is normally 5.0 % to 13.0 % aluminium, 2.0 % to 4.0 % magnesium, 1.0 % other elements and the balance zinc.
JIS G 3323:2012 Referenced Document
JIS G 0320 Standard test method for heat analysis of steel products
JIS G 0404 Steel and steel products -- General technical delivery requirements*, 2023-12-20 Update
JIS G 0415 Steel and steel products -- Inspection documents*, 2014-05-20 Update
JIS G 0594 Methods of accelerated cyclic corrosion tests for surface treated steel sheet*, 2019-06-20 Update
JIS G 3316 Shapes and dimensions of corrugated steel sheets*, 2019-01-01 Update
JIS H 0401 Test methods for hot dip galvanized coatings*, 2021-12-20 Update
JIS H 8502 Methods of corrosion resistance test for metallic coatings
JIS K 0119 General rules for X-ray fluorescence analysis
JIS K 5600-7-9 Testing methods for paints -- Part 7: Determination of resistance to cyclic corrosion conditions -- Section 9: Salt fog/dry/humidity
JIS Z 2241 Metallic materials -- Tensile testing -- Method of test at room temperature*, 2022-09-20 Update
JIS Z 8401 Rounding of numbers*, 2019-01-01 Update
JIS G 3323:2012 history
2022JIS G 3323:2022 Hot-dip zinc-aluminium-magnesium alloy-coated steel sheet and strip
2019JIS G 3323:2019 Hot-dip zinc-aluminium-magnesium alloy-coated steel sheet and strip
2012JIS G 3323:2012 Hot-dip zinc-aluminium-magnesium alloy-coated steel sheet and strip