ASTM C810-90(2011)e1
Standard Test Method for Nickel on Steel for Porcelain Enameling by X-Ray Emission Spectrometry

Standard No.

ASTM C810-90(2011)e1

Release Date

1990

Published By

American Society for Testing and Materials (ASTM)

Status

Be replaced

Replace By

ASTM C810-90(2016)

Latest

ASTM C810-90(2016)

Scope

This test method is an accurate and rapid means for measuring nickel deposits on steel sample plates and such parts that can be fitted into the X-ray spectrometer. Its accuracy extends over a wide range of nickel deposits.

1.1 This test method covers the measurement of the amount of nickel deposited on sheet steel during its preparation for porcelain enameling. It is an X-ray emission method used for testing sample panels or certain commercial parts.

Note 18212;An alternative wet chemical method is Test Method C715.

1.2 The values stated in inch-pound units are to be regarded as the standard. The values given in parentheses are for information only.

ASTM C810-90(2011)e1 history

• 1970 ASTM C810-90(2016) Standard Test Method for Nickel on Steel for Porcelain Enameling by X-Ray Emission Spectrometry
• 1990 ASTM C810-90(2011)e1 Standard Test Method for Nickel on Steel for Porcelain Enameling by X-Ray Emission Spectrometry
• 1990 ASTM C810-90(2006) Standard Test Method for Nickel on Steel for Porcelain Enameling by X-Ray Emission Spectrometry
• 1990 ASTM C810-90(2000) Standard Test Method for Nickel on Steel for Porcelain Enameling by X-Ray Emission Spectrometry
• 2000 ASTM C810-90(1995) Standard Test Method for Nickel on Steel for Porcelain Enameling by X-Ray Emission Spectrometry