ISO 9591:2004 PDF

Scope: 1 This International Standard specifies a method for the determination of resistance to stress corrosion cracking (SCC) of aluminium alloys. 2 This International Standard covers the method of sampling, the types of specimens, the loading procedure, the type of environment and the interpretation of results. 3 This International Standard is aimed at determining resistance to SCC as a function of the chemical composition, the method of manufacture and heat treatment of aluminium alloys. 4 This International Standard applies to cast and wrought aluminium alloys in the form of castings, semi-finished products, parts and weldments. 5 Since most natural and many artificial environments contain chlorides, this International Standard can be used to compare the performance of products employed under marine atmospheres and in environments containing chlorides, providing that the failure mechanism is not changed. However, the results of this test should not be considered as an absolute criterion for the quality of alloys.

ISO 9591:2004 Referenced Document

ISO 7539-3 Corrosion of metals and alloys; stress corrosion testing; part 3: preparation and use of U-bend specimens
ISO 7539-8:2000 Corrosion of metals and alloys - Stress corrosion testing - Part 8: Preparation and use of specimens to evaluate weldments
ISO 7539-9:2003 Corrosion of metals and alloys - Stress corrosion testing - Part 9: Preparation and use of pre-cracked specimens for tests under rising load or rising displacement

2004 ISO 9591:2004 Corrosion of aluminium alloys - Determination of resistance to stress corrosion cracking
1992 ISO 9591:1992 Corrosion of aluminium alloys; determination of resistance to stress corrosion cracking