DIN EN ISO 18592:2010 Resistance welding - Destructive testing of welds - Method for the fatigue testing of multi-spot-welded specimens (ISO 18592:2009); German version EN ISO 18592:2009
This document specifies test specimens and procedures for performing constant load amplitude fatigue tests on multi-spot-welded- and multi-axial-specimens specimens in the thickness range from 0, 5 mm to 4, 5 mm at room temperature and a relative humidity of max. 80 %. The applicability of the standard to larger thicknesses may be limited by the mechanical properties such as yield strength and formability of the specimen material. The thickness range for Advanced High Strength Steels (AHSS) is generally below 3, 0 mm. Greater thicknesses for e. g. aluminium alloys are permissible. The test results of the fatigue tests may also be used for deriving criteria for the selection of materials and thickness combinations for structures and components subjected to cyclic loading. This statement is relevant for results obtained with component like specimens, i.e. specimens with a local stiffness similar to that of structural components. The results of a fatigue test are suitable for direct application to design only when the loading conditions in service and the stiffness of the design in the joint area are identical.
DIN EN ISO 18592:2010 Referenced Document
ISO 14273 Resistance welding - Destructive testing of welds - Specimen dimensions and procedure for tensile shear testing resistance spot and embossed projection welds*, 2016-03-01 Update
ISO 14324 Resistance spot welding - Destructive tests of welds - Method for the fatigue testing of spot welded joints
ISO 15609-5:2004 Specification and qualification of welding procedures for metallic materials - Welding procedure specification - Part 5: Resistance welding
DIN EN ISO 18592:2010 history
2019DIN EN ISO 18592:2019-12 Resistance welding - Destructive testing of welds - Method for the fatigue testing of multi-spot-welded specimens (ISO 18592:2019); German version EN ISO 18592:2019
2019DIN EN ISO 18592:2019 Resistance welding - Destructive testing of welds - Method for the fatigue testing of multi-spot-welded specimens (ISO 18592:2019)
1970DIN EN ISO 18592 E:2017-04 Method for destructive testing of resistance welded joints and fatigue testing of multi-point welded samples (draft)
2017DIN EN ISO 18592 E:2017 Draft Document - Resistance welding - Destructive testing of welds - Method for the fatigue testing of multi-spot-welded specimens (ISO/DIS 18592:2017); German and English version prEN ISO 18592:2017
2010DIN EN ISO 18592:2010 Resistance welding - Destructive testing of welds - Method for the fatigue testing of multi-spot-welded specimens (ISO 18592:2009); German version EN ISO 18592:2009