ASTM A395/A395M-99(2009)
Standard Specification for Ferritic Ductile Iron Pressure-Retaining Castings for Use at Elevated Temperatures
- Standard No.
- ASTM A395/A395M-99(2009)
- Release Date
- 1999
- Published By
- American Society for Testing and Materials (ASTM)
- Status
- Replace By
- ASTM A395/A395M-99(2014)
- Latest
- ASTM A395/A395M-99(2022)
- Scope
1.1 This specification covers ductile iron castings for pressure-retaining parts for use at elevated temperatures. Castings of all grades are suitable for use up to 450°F. For temperatures above 450°F and up to 650°F, only Grade 60–40–18 castings are suitable (Note 1).
1.2 Valves, flanges, pipe fittings, pumps, and other piping components are generally manufactured in advance and supplied from stock by the manufacturer, jobber, or dealer.
1.3 For supplemental casting requirements, Specification A 834
may be utilized. 1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.
Note 18212;For service other than as specified in this section, reference should be made to Specification A 536
for Ductile Iron Castings.
ASTM A395/A395M-99(2009) Referenced Document
- ASTM A247 Standard Test Method for Evaluating the Microstructure of Graphite in Iron Castings
- ASTM A370 Standard Test Methods and Definitions for Mechanical Testing of Steel Products*， 2001-12-10 Update
- ASTM A536 Standard Specification for Ductile Iron Castings*， 2009-05-01 Update
- ASTM A834 Standard Specification for Common Requirements for Iron Castings for General Industrial Use*， 2020-05-01 Update
- ASTM E10 Standard Test Method for Brinell Hardness of Metallic Materials*， 2023-08-03 Update
- ASTM E1806 Standard Practice for Sampling Steel and Iron for Determination of Chemical Composition*， 2006-11-01 Update
- ASTM E186 Standard Reference Radiographs for Heavy-Walled (2 to 4 &189; in. [51 to 114-mm]) Steel Castings
- ASTM E280 Standard Reference Radiographs for Heavy-Walled (4 &189; to 12-in. [114 to 305-mm]) Steel Castings
- ASTM E446 Standard Reference Radiographs for Steel Castings Up to 2 in. [51 mm] in Thickness
- ASTM E689 Standard Reference Radiographs for Ductile Iron Castings
- ASTM E8 Standard Test Methods for Tension Testing of Metallic Materials
- ASTM F1476 Standard Specification for Performance of Gasketed Mechanical Couplings for Use in Piping Applications
- ASTM F1548 Standard Specification for the Performance of Fittings for Use with Gasketed Mechanical Couplings Used in Piping Applications
ASTM A395/A395M-99(2009) history
- 2022 ASTM A395/A395M-99(2022) Standard Specification for Ferritic Ductile Iron Pressure-Retaining Castings for Use at Elevated Temperatures
- 2018 ASTM A395/A395M-99(2018) Standard Specification for Ferritic Ductile Iron Pressure-Retaining Castings for Use at Elevated Temperatures
- 1999 ASTM A395/A395M-99(2014) Standard Specification for Ferritic Ductile Iron Pressure-Retaining Castings for Use at Elevated Temperatures
- 1999 ASTM A395/A395M-99(2009) Standard Specification for Ferritic Ductile Iron Pressure-Retaining Castings for Use at Elevated Temperatures
- 1999 ASTM A395/A395M-99(2004) Standard Specification for Ferritic Ductile Iron Pressure-Retaining Castings for Use at Elevated Temperatures
- 1999 ASTM A395/A395M-99e1 Standard Specification for Ferritic Ductile Iron Pressure-Retaining Castings for Use at Elevated Temperatures
- 1999 ASTM A395/A395M-99 Standard Specification for Ferritic Ductile Iron Pressure-Retaining Castings for Use at Elevated Temperatures
- 1998 ASTM A395/A395M-98 Standard Specification for Ferritic Ductile Iron Pressure-Retaining Castings for Use at Elevated Temperatures
- 1988 ASTM A395-88 Standard Specification For Ferritic Ductile Iron Pressure-Retaining Castings For Use At Elevated Temperatures - WITHDRAWN - Replaced by ASTM A395/A395M-98
- 1968 ASTM A395-68 Standard Specifications For Ductile Iron For Pressure Containing Castings For Use At Elevated Temperatures