DIN EN ISO 13807:2009
Vitreous and porcelain enamels - Determination of crack formation temperature in the thermal shock testing of enamels for the chemical industry (ISO 13807:1999, including Cor 1:2000); English version of DIN EN ISO 13807:2009-04
- Standard No.
- DIN EN ISO 13807:2009
- Release Date
- 2009
- Published By
- German Institute for Standardization
- Status
- Replace By
- DIN EN ISO 13807 E:2022-02
- Latest
- DIN EN ISO 13807:2023-01
- Replace
- DIN ISO 13807:2001 DIN EN ISO 13807:2008
- Scope
- This International Standard specifies a test method for the determination of the crack formation temperature of enamels for the chemical industry by subjecting enamelled steel specimens to thermal shock using cold water. The value of the crack formation temperature measured according to this test method is not valid for the finished component (see annex A). It is a parameter of vitreous and porcelain enamels for comparing the relative quality of different enamel formulations.
DIN EN ISO 13807:2009 Referenced Document
- ISO 2746 Vitreous and porcelain enamels - High voltage test*， 2015-10-01 Update
- ISO 2808 Paints and varnishes — Determination of film thickness*， 2019-07-26 Update
- ISO 3819 Laboratory glassware - Beakers*， 2015-12-01 Update
DIN EN ISO 13807:2009 history
- 2023 DIN EN ISO 13807:2023-01 Vitreous and porcelain enamels - Determination of crack formation temperature in the thermal shock testing of enamels for the chemical industry (ISO 13807:2022); German version EN ISO 13807:2022
- 1970 DIN EN ISO 13807 E:2022-02 Determination of crack formation temperature in thermal shock tests on enamels and enamel-chemical industries (draft)
- 2009 DIN EN ISO 13807:2009 Vitreous and porcelain enamels - Determination of crack formation temperature in the thermal shock testing of enamels for the chemical industry (ISO 13807:1999, including Cor 1:2000); English version of DIN EN ISO 13807:2009-04
- 0000 DIN EN ISO 13807:2008
- 0000 DIN ISO 13807:2001