ASTM D1654-08
Standard Test Method for Evaluation of Painted or Coated Specimens Subjected to Corrosive Environments

Standard No.

ASTM D1654-08

Release Date

2008

Published By

American Society for Testing and Materials (ASTM)

Status

Be replaced

Replace By

ASTM D1654-08(2016)

Latest

ASTM D1654-08(2016)e1

Scope

This method provides a means of evaluating and comparing basic corrosion performance of the substrate, pretreatment, or coating system, or combination thereof, after exposure to corrosive environments.

1.1 This test method covers the treatment of previously painted or coated specimens for accelerated and atmospheric exposure tests and their subsequent evaluation in respect to corrosion, blistering associated with corrosion, loss of adhesion at a scribe mark, or other film failure.

1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.

1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of whoever uses this standard to consult and establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ASTM D1654-08 Referenced Document

• ASTM B117 Standard Practice for Operating Salt Spray (Fog) Apparatus
• ASTM D1014 Standard Practice for Conducting Exterior Exposure Tests of Paints on Steel
• ASTM D1735 Standard Practice for Testing Water Resistance of Coatings Using Water Fog Apparatus
• ASTM D2247 Standard Practice for Testing Water Resistance of Coatings in 100% Relative Humidity
• ASTM D2803 Standard Guide for Testing Filiform Corrosion Resistance of Organic Coatings on Metal
• ASTM D4141 Standard Practice for Conducting Black Box and Solar Concentrating Exposures of Coatings
• ASTM D4585 Standard Practice for Testing Water Resistance of Coatings Using Controlled Condensation
• ASTM D4587 Standard Practice for Fluorescent UV-Condensation Exposures of Paint and Related Coatings
• ASTM D5894 Standard Practice for Cyclic Salt Fog/UV Exposure of Painted Metal, (Alternating Exposures in a Fog/Dry Cabinet and a UV/Condensation Cabinet)
• ASTM D610 Standard Test Method for Evaluating Degree of Rusting on Painted Steel Surfaces
• ASTM D6695 Standard Practice for Xenon-Arc Exposures of Paint and Related Coatings*， 2024-04-19 Update
• ASTM D7087 Standard Test Method for An Imaging Technique to Measure Rust Creepage at Scribe on Coated Test Panels Subjected to Corrosive Environments
• ASTM D714 Standard Test Method for Evaluating Degree of Blistering of Paints
• ASTM D822 Standard Practice for Filtered Open-Flame Carbon-Arc Exposures of Paint and Related Coatings
• ASTM D870 Standard Practice for Testing Water Resistance of Coatings Using Water Immersion
• ASTM E3 Standard Practice for Preparation of Metallographic Specimens
• ASTM G85 Standard Practice for Modified Salt Spray (Fog) Testing
• ASTM G87 Standard Practice for Conducting Moist SO₂ Tests

ASTM D1654-08 history

• 2016 ASTM D1654-08(2016)e1 Standard test method for evaluating coatings or coating samples for corrosive environments
• 2016 ASTM D1654-08(2016) Standard Test Method for Evaluation of Painted or Coated Specimens Subjected to Corrosive Environments
• 2008 ASTM D1654-08 Standard Test Method for Evaluation of Painted or Coated Specimens Subjected to Corrosive Environments
• 2005 ASTM D1654-05 Standard Test Method for Evaluation of Painted or Coated Specimens Subjected to Corrosive Environments
• 1992 ASTM D1654-92(2000) Standard Test Method for Evaluation of Painted or Coated Specimens Subjected to Corrosive Environments