SAE AMS4310E-2008
Aluminum Alloy, Rolled or Forged Rings, 5.6Zn-2.5Mg-1.6Cu-0.23Cr (7075-T651, 7075-T652) Solution Heat Treated, Mechanically Stress Relieved, and Precipitation Heat Treated

Standard No.

SAE AMS4310E-2008

Release Date

2008

Published By

Society of Automotive Engineers (SAE)

Status

Be replaced

Replace By

SAE AMS4310E-2013

Latest

SAE AMS4310F-2020

Scope

1.1 FormThis specification covers an aluminum alloy in the form of rolled or forged rings.1.2 ApplicationThese rings have been used typically for high strength machined parts where good stability is required during machining,but usage is not limited to such applications. These rings are not recommended for fusion welding.1.2.1 Certain design and fabricating procedures may cause these rings to become susceptible to stress-corrosion cracking; ARP823 recommends practices to minimize such conditions.1.3 ClassificationRings are classified by type of mechanical stress relief as follows:7075-T651 Stress relieved by tension7075-T652 Stress relieved by compression1.3.1 Either type may be supplied, unless a specific type is ordered.

SAE AMS4310E-2008 Referenced Document

• ASTM B594 Standard Practice for Ultrasonic Inspection of Aluminum-Alloy Wrought Products for Aerospace Applications
• ASTM B660 Standard Practices for Packaging/Packing of Aluminum and Magnesium Products
• SAE AMS2355 TENSILE TESTING OF WROUGHT ALUMINUM AND MAGNESIUM PRODUCTS Except Forgings
• SAE AMS2772 Heat Treatment of Aluminum Alloy Raw Materials (01 1997)
• SAE AMS2808 IDENTIFICATION Forgings
• SAE ARP823 MINIMIZING STRESS CORROSION IN WROUGHT HEAT TREATABLE ALUMINUM ALLOY PRODUCTS

SAE AMS4310E-2008 history

• 2020 SAE AMS4310F-2020 Aluminum Alloy, Rolled or Forged Rings 5.6Zn - 2.5Mg - 1.6Cu - 0.23Cr (7075-T651, 7075-T652) Solution Heat Treated, Mechanically Stress Relieved, and Precipitation Heat Treated (UNS A97075)
• 2013 SAE AMS4310E-2013 Aluminum Alloy, Rolled or Forged Rings 5.6Zn - 2.5Mg - 1.6Cu - 0.23Cr (7075-T651, 7075-T652) Solution Heat Treated, Mechanically Stress Relieved, and Precipitation Heat Treated
• 2008 SAE AMS4310E-2008 Aluminum Alloy, Rolled or Forged Rings, 5.6Zn-2.5Mg-1.6Cu-0.23Cr (7075-T651, 7075-T652) Solution Heat Treated, Mechanically Stress Relieved, and Precipitation Heat Treated
• 2006 SAE AMS4310D-2006 Aluminum Alloy, Rolled or Forged Rings 5.6Zn - 2.5Mg - 1.6Cu - 0.23Cr (7075-T651, 7075-T652) Solution Heat Treated, Mechanically Stress Relieved, and Precipitation Heat Treated
• 2001 SAE AMS4310D-2001 Aluminum Alloy, Rolled or Forged Rings, 5.6Zn 2.5Mg 1.6Cu 0.23Cr (7075-T651, 7075-T652) Solution Heat Treated, Mechanically Stress Relieved, and Precipitation Heat Treated
• 1994 SAE AMS4310C-1994 Aluminum Alloy@ Rolled or Forged Rings 5.6Zn - 2.5Mg - 1.6Cu - 0.23Cr (7075-T651@ 7075-T652) Solution Heat Treated@ Mechanically Stress Relieved@ and Precipitation Heat Treated (UNS A97075)
• 1988 SAE AMS4310B-1988 ALUMINUM ALLOY RINGS@ ROLLED OR FORGED 5.6Zn - 2.5Mg - 1.6Cu - 0.23Cr (7075-T651@ 7075-T652) Solution Heat Treated@ Mechanically Stress Relieved@ and Precipitation Heat Treated (UNS A97075)
• 1983 SAE AMS4310A-1983 ALUMINUM ALLOY RINGS@ ROLLED OR FORGED 5.6Zn - 2.5Mg - 1.6Cu - 0.23Cr (7075-T651@ 7075-T652) Solution Heat Treated@ Mechanically Stress Relieved@ and Precipitation Heat Treated (UNS A97075)
• 1976 SAE AMS4310-1976 ALUMINUM ALLOY RINGS@ ROLLED OR FORGED 5.6Zn - 2.5Mg - 1.6Cu - 0.26Cr (7075-T651@ 7075-T652) Mechanically Stress Relieved (UNS A97075)