DIN EN ISO 16701:2008 PDF

Scope: This International Standard defines an accelerated corrosion test method to be used in assessing the corrosion resistance of metals in environments where there is a significant influence of chloride ions, mainly as sodium chloride from a marine source or road de-icing salt. This International Standard specifies the test apparatus and test procedure to be used in conducting the accelerated corrosion test to simulate, in a very controlled way, atmospheric corrosion conditions. In this International Standard, the term "metal" includes metallic materials with or without corrosion protection. The accelerated laboratory corrosion test applies to -- metals and their alloys; -- metallic coatings (anodic and cathodic); -- chemical conversion coatings; -- organic coatings on metals. The method is especially suitable for comparative testing in the optimization of surface treatment systems.

DIN EN ISO 16701:2008 Referenced Document

ISO 10289 Methods for corrosion testing of metallic and other inorganic coatings on metallic substrates - Rating of test specimens and manufactured articles subjected to corrosion tests
ISO 4628-1 Paints and varnishes - Evaluation of degradation of coatings - Designation of quantity and size of defects, and of intensity of uniform changes in appearance - Part 1: General introduction and designation system*， 2016-01-01 Update
ISO 4628-2 Paints and varnishes - Evaluation of degradation of coatings - Designation of quantity and size of defects, and of intensity of uniform changes in appearance - Part 2: Assessment of degree of blistering*， 2016-01-01 Update
ISO 4628-4 Paints and varnishes - Evaluation of degradation of coatings - Designation of quantity and size of defects, and of intensity of uniform changes in appearance - Part 4: Assessment of degree of cracking*， 2016-01-01 Update
ISO 4628-5 Paints and varnishes — Evaluation of quantity and size of defects, and of intensity of uniform changes in appearance — Part 5: Assessment of degree of flaking*， 2022-11-11 Update
ISO 8407 Corrosion of metals and alloys*， 2024-01-01 Update

2023 DIN EN ISO 16701:2023-10 Corrosion of metals and alloys - Corrosion in artificial atmosphere - Accelerated corrosion test involving exposure under controlled conditions of humidity cycling and intermittent spraying of a salt solution (ISO/DIS 16701:2023); German and English ve...
2015 DIN EN ISO 16701:2015-10 Corrosion of metals and alloys - Corrosion in artificial atmosphere - Accelerated corrosion test involving exposure under controlled conditions of humidity cycling and intermittent spraying of a salt solution (ISO 16701:2015); German version EN ISO 167...
2015 DIN EN ISO 16701:2015 Corrosion of metals and alloys - Corrosion in artificial atmosphere - Accelerated corrosion test involving exposure under controlled conditions of humidity cycling and intermittent spraying of a salt solution (ISO 16701:2015); German version EN ISO 16701:
2008 DIN EN ISO 16701:2008 Corrosion of metals and alloys - Corrosion in artificial atmosphere - Accelerated corrosion test involving exposure under controlled conditions of humidity cycling and intermittent spraying of a salt solution (ISO 16701:2003); German version EN ISO 16701:
0000 DIN EN ISO 16701:2007