ASTM C416-97(2007)
Standard Classification of Silica Refractory Brick
- Standard No.
- ASTM C416-97(2007)
- Release Date
- 1997
- Published By
- American Society for Testing and Materials (ASTM)
- Status
- Replace By
- ASTM C416-97(2013)
- Latest
- ASTM C416-97(2022)
- Scope
The presence of certain impurities in silica brick tends to lower their refractoriness and service limits. This classification permits those familiar with refractories to predict the refractoriness of silica brick from their alkali and alumina contents.
1.1 This classification is limited to silica brick meeting the following requirements:Alumina (Al
2 O3 ) content of less than 1.50 %.Titania (TiO2 ) content of less than 0.20 %.Iron oxide (FeO3 ) content of less than 2.50 %.Calcium oxide (CaO) content of less than 4.00 %.Average modulus of rupture of not less than 500 psi (3.45 MPa).1.2 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
ASTM C416-97(2007) Referenced Document
- ASTM C133 Standard Test Methods for Cold Crushing Strength and Modulus of Rupture of Refractories*， 2024-04-19 Update
ASTM C416-97(2007) history
- 2022 ASTM C416-97(2022) Standard Classification of Silica Refractory Brick
- 2018 ASTM C416-97(2018) Standard Classification of Silica Refractory Brick
- 1997 ASTM C416-97(2013) Standard Classification of Silica Refractory Brick
- 1997 ASTM C416-97(2007) Standard Classification of Silica Refractory Brick
- 1997 ASTM C416-97(2002) Standard Classification of Silica Refractory Brick
- 1997 ASTM C416-97 Standard Classification of Silica Refractory Brick