ASTM A608-91a(1998)
Standard Specification for Centrifugally Cast Iron-Chromium-Nickel High-Alloy Tubing for Pressure Application at High Temperatures

Standard No.

ASTM A608-91a(1998)

Release Date

1991

Published By

American Society for Testing and Materials (ASTM)

Status

Be replaced

Replace By

ASTM A608/A608M-02

Latest

ASTM A608/A608M-20

Scope

1.1 This specification covers iron-chromium-nickel, high-alloy tubes made by the centrifugal casting process intended for use under pressure at high temperatures.

1.2 The grades of high alloys detailed in Table 1 are intended for applications requiring strength and resistance to corrosion and scaling at high temperatures.

1.3 Optional Supplementary Requirements S1 to S11 are provided; these call for additional tests to be made if desired.

1.4 The values stated in inch-pound units are to be regarded as the standard.

ASTM A608-91a(1998) history

• 2020 ASTM A608/A608M-20 Standard Specification for Centrifugally Cast Iron-Chromium-Nickel High-Alloy Tubing for Pressure Application at High Temperatures
• 2018 ASTM A608/A608M-14(2018) Standard Specification for Centrifugally Cast Iron-Chromium-Nickel High-Alloy Tubing for Pressure Application at High Temperatures
• 2014 ASTM A608/A608M-14 Standard Specification for Centrifugally Cast Iron-Chromium-Nickel High-Alloy Tubing for Pressure Application at High Temperatures
• 2012 ASTM A608/A608M-12 Standard Specification for Centrifugally Cast Iron-Chromium-Nickel High-Alloy Tubing for Pressure Application at High Temperatures
• 2006 ASTM A608/A608M-06(2012) Standard Specification for Centrifugally Cast Iron-Chromium-Nickel High-Alloy Tubing for Pressure Application at High Temperatures
• 2006 ASTM A608/A608M-06 Standard Specification for Centrifugally Cast Iron-Chromium-Nickel High-Alloy Tubing for Pressure Application at High Temperature
• 2002 ASTM A608/A608M-02 Standard Specification for Centrifugally Cast Iron-Chromium-Nickel High-Alloy Tubing for Pressure Application at High Temperatures
• 1991 ASTM A608-91a(1998) Standard Specification for Centrifugally Cast Iron-Chromium-Nickel High-Alloy Tubing for Pressure Application at High Temperatures