ASTM C928-05
Standard Specification for Packaged, Dry, Rapid-Hardening Cementitious Materials for Concrete Repairs
- Standard No.
- ASTM C928-05
- Release Date
- 2005
- Published By
- American Society for Testing and Materials (ASTM)
- Status
- Replace By
- ASTM C928/C928M-08
- Latest
- ASTM C928/C928M-20a
- Scope
1.1 This specification covers packaged, dry, cementitious mortar or concrete materials for rapid repairs to hardened hydraulic-cement concrete pavements and structures. Materials that contain organic compounds, such as bitumens, epoxy resins, and polyesters, as the principal binder are not included.
1.1.1 Packaged, dry, concrete material contains aggregate of which at least 5 % by mass of the total mixture is retained on a 9.5-mm (3/8-in.) sieve.
1.1.2 Packaged, dry, mortar material contains aggregate of which less than 5 % by mass of the total mixture is retained on a 9.5-mm (3/8-in.) sieve.
1.2 Aqueous solutions, aqueous emulsions or dispersions may be included as components of the packaged materials. The manufacturer may specify that these liquids are to replace some or all of the mixing water.
1.3 Aggregates must be included as a component of the packaged materials. The manufacturer may recommend job site addition of specific amounts and types of additional aggregates to his product for some uses. However, such reformulated products are not within the scope of this specification.
1.4 The values stated in SI units are to be regarded as standard. The inch-pound units given in parentheses are for information only. Values in SI units shall be obtained by measurement in SI units or by appropriate conversion of measurements made in other units, using the Rules for Conversion and Rounding given in IEEE/ASTM SI-10.
1.5
The following safety hazards caveat pertains to the test methods portion of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
ASTM C928-05 Referenced Document
- ASTM C1012 Standard Test Method for Length Change of Hydraulic-Cement Mortars Exposed to a Sulfate Solution
- ASTM C143 Standard Test Method for Slump Of Portland Cement Concrete
- ASTM C157 Standard Test Method for Length Change Of Hardened Cement Mortar And Concrete
- ASTM C39/C39M Standard Test Method for Compressive Strength of Cylindrical Concrete Specimens
- ASTM C494 Standard Specification for Chemical Admixtures For Concrete
- ASTM C666 Standard Test Method for Resistance of Concrete to Rapid Freezing and Thawing
- ASTM C702 Standard Practice for Reducing Samples of Aggregate to Testing Size
- ASTM C78 Standard Test Method for Flexural Strength of Concrete (Using Simple Beam with Third-Point Loading)
- ASTM C882 Standard Test Method for Bond Strength of Epoxy-Resin Systems Used With Concrete By Slant Shear
- ASTM E96 Standard Test Method for Water Vapor Transmission of Materials
- IEEE/ASTM SI 10 American National Standard for Metric Practice
ASTM C928-05 history
- 2020 ASTM C928/C928M-20a Standard Specification for Packaged, Dry, Rapid-Hardening Cementitious Materials for Concrete Repairs
- 2020 ASTM C928/C928M-20 Standard Specification for Packaged, Dry, Rapid-Hardening Cementitious Materials for Concrete Repairs
- 2019 ASTM C928/C928M-19 Standard Specification for Packaged, Dry, Rapid-Hardening Cementitious Materials for Concrete Repairs
- 2013 ASTM C928/C928M-13 Standard Specification for Packaged, Dry, Rapid-Hardening Cementitious Materials for Concrete Repairs
- 2009 ASTM C928/C928M-09 Standard Specification for Packaged, Dry, Rapid-Hardening Cementitious Materials for Concrete Repairs
- 2008 ASTM C928/C928M-08 Standard Specification for Packaged, Dry, Rapid-Hardening Cementitious Materials for Concrete Repairs
- 2005 ASTM C928-05 Standard Specification for Packaged, Dry, Rapid-Hardening Cementitious Materials for Concrete Repairs
- 2000 ASTM C928-00 Standard Specification for Packaged, Dry, Rapid-Hardening Cementitious Materials for Concrete Repairs