ASTM B78-90(1995)e1
Standard Test Method of Accelerated Life of Iron-Chromium-Aluminum Alloys for Electrical Heating

Standard No.

ASTM B78-90(1995)e1

Release Date

1990

Published By

American Society for Testing and Materials (ASTM)

Status

Be replaced

Replace By

ASTM B78-90(2001)

Latest

ASTM B78-90(2019)

Scope

1.1 This test method covers the determination of the resistance to oxidation of iron-chromium-aluminum electrical heating alloys at elevated temperatures under intermittent heating using a constant-temperature cycle test. This test is used for internal comparative purposes only.

1.2 The values stated in inch-pound units are to be regarded as the standard. The metric equivalents of inch-pound units may be approximate.

1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ASTM B78-90(1995)e1 history

• 2019 ASTM B78-90(2019) Standard Test Method of Accelerated Life of Iron-Chromium-Aluminum Alloys for Electrical Heating
• 1990 ASTM B78-90(2013) Standard Test Method of Accelerated Life of Iron-Chromium-Aluminum Alloys for Electrical Heating
• 1990 ASTM B78-90(2007) Standard Test Method of Accelerated Life of Iron-Chromium-Aluminum Alloys for Electrical Heating
• 1990 ASTM B78-90(2001) Standard Test Method of Accelerated Life of Iron-Chromium-Aluminum Alloys for Electrical Heating
• 1990 ASTM B78-90(1995)e1 Standard Test Method of Accelerated Life of Iron-Chromium-Aluminum Alloys for Electrical Heating