This part of YY 0605 specifies the characteristics and corresponding test methods of stainless steel for surgical implants with a nitrogen content of 0.25% to 0.5%, high strength and good corrosion resistance.
YY 0605.9-2007 Referenced Document
GB/T 10561 Standard grading chart microscopic examination method for determination of non-metallic inclusion content in steel*, 2023-05-23 Update
GB/T 228 Metallic materials--Tensile testing at ambient temperature
GB/T 2975 Steel and steel products.Location and preparation of samples and test pieces for mechanical testing*, 2018-05-14 Update
ISO 10714:1992 Steel and iron; determination of phosphorus content; phosphovanadomolybdate spectrophotometric method
ISO 3651-2:1976 Austenitic stainless steels; Determination of resistance to intergranular corrosion; Part II : Corrosion test in a sulphuric acid/copper sulphate medium in the presence of copper turnings (Monypenny Strauss test)
ISO 404:1981 Steel and steel products — General technical delivery requirements
ISO 437:1982 Steel and cast iron; Determination of total carbon content; Combustion gravimetric method
ISO 439:1994 Steel and iron; determination of total silicon content; gravimetric method
ISO 629:1982 Steel and cast iron; Determination of manganese content; Spectrophotometric method
ISO 643:1983 Steels; Micrographic determination of the ferritic or austenitic grain size
ISO 671:1982 Steel and cast iron; Determination of sulphur content; Combustion titrimetric method
YY 0605.9-2007 history
2015YY 0605.9-2015 Implants for surgery.Metallic materials.Part 9:Wrought high nitrogen stainless steel
2007YY 0605.9-2007 Implants for surgery-Metallic materials-Part 9: Wrought high nitrogen stainless steel