GB/T 20853-2007 Corrosion of metals and alloys Corrosion in artificial atmosphere Accelerated corrosion test involving exposure under controlled conditions of humidity cycling and intermittent sprayingof a salt solution (English Version)
General Administration of Quality Supervision, Inspection and Quarantine of the People‘s Republic of China
Latest
GB/T 20853-2007
Scope
This standard specifies a test method for the resistance of metals to corrosion in the presence of chloride ions, primarily sodium chloride derived from marine and road deicing salts. This standard specifies equipment and test procedures for accelerated corrosion testing that simulates atmospheric corrosion conditions in a highly controlled manner. Metals in this standard include metal materials with corrosion protection and without corrosion protection. This laboratory accelerated corrosion test is applicable to: - metals and their alloys; - metallic coatings (anodic and cathodic); - chemical conversion coatings; - organic coatings on metals. It is especially suitable for comparative experiments on the optimization of surface treatment methods.
GB/T 20853-2007 Referenced Document
GB/T 16545 Corrosion of metals and alloys.Removal of corrosion products from corrosion test specimens*, 2015-09-11 Update
GB/T 6461 Methods for corrosion testing of metallic and other inorganic coatings on metallic substrates--Rating of test specimens and manufactured articles subjected to corrosion tests
ISO 4628-1 Paints and varnishes - Evaluation of degradation of coatings - Designation of quantity and size of defects, and of intensity of uniform changes in appearance - Part 1: General introduction and designation system*, 2016-01-01 Update
ISO 4628-2 Paints and varnishes - Evaluation of degradation of coatings - Designation of quantity and size of defects, and of intensity of uniform changes in appearance - Part 2: Assessment of degree of blistering*, 2016-01-01 Update
ISO 4628-4 Paints and varnishes - Evaluation of degradation of coatings - Designation of quantity and size of defects, and of intensity of uniform changes in appearance - Part 4: Assessment of degree of cracking*, 2016-01-01 Update
ISO 4628-5 Paints and varnishes — Evaluation of quantity and size of defects, and of intensity of uniform changes in appearance — Part 5: Assessment of degree of flaking*, 2022-11-11 Update
GB/T 20853-2007 history
2007GB/T 20853-2007 Corrosion of metals and alloys Corrosion in artificial atmosphere Accelerated corrosion test involving exposure under controlled conditions of humidity cycling and intermittent sprayingof a salt solution