SAE AMS6317G-2003
Steel Bars and Forgings 1.8Ni 0.25Mo (0.38-0.43C) (4640) Heat Treated, 125 ksi (862 MPa) Tensile Strength

Standard No.

SAE AMS6317G-2003

Release Date

2003

Published By

Society of Automotive Engineers (SAE)

Status

Withdraw

Replace By

SAE AMS6317H-2007

Latest

SAE AMS6317L-2022

Scope

This specification covers an aircraft-quality, low-alloy steel in the form of heat treated bars and forgings. These products have been used typically for parts with sections 1.0 inch (25 mm) and under in nominal thickness requiring a minimum tensile strength of 125 ksi (862 MPa), but usage is not limited to such applications.

SAE AMS6317G-2003 history

• 2022 SAE AMS6317L-2022 Steel Bars and Forgings 1.8Ni - 0.25Mo (0.38 - 0.43C) (4640) Heat Treated, 125 ksi (862 MPa) Tensile Strength
• 2017 SAE AMS6317K-2017 Steel Bars and Forgings 1.8Ni - 0.25Mo (0.38 - 0.43C) (4640) Heat Treated@ 125 ksi (862 MPa) Tensile Strength (UNS K22440)
• 2012 SAE AMS6317J-2012 Steel Bars and Forgings 1.8Ni 0.25Mo (0.38-0.43C) (4640) Heat Treated, 125 ksi (862 MPa) Tensile Strength
• 2007 SAE AMS6317H-2007 Steel Bars and Forgings 1.8Ni - 0.25Mo (0.38 - 0.43C) (4640) Heat Treated, 125 ksi (862 MPa) Tensile Strength UNS K22440
• 2003 SAE AMS6317G-2003 Steel Bars and Forgings 1.8Ni 0.25Mo (0.38-0.43C) (4640) Heat Treated, 125 ksi (862 MPa) Tensile Strength
• 1995 SAE AMS6317F-1995 STEEL BARS AND FORGINGS 1.8Ni - 0.25Mo (0.38 - 0.43C) (4640) Heat Treated, 125 ksi (862 MPa) Tensile Strength
• 1991 SAE AMS6317F-1991 Steel Bars and Forgings 1.8Ni - 0.25Mo (0.38 - 0.43C) (4640) Heat Treated@ 125 ksi (862 MPa) Tensile Strength
• 1986 SAE AMS6317E-1986 STEEL BARS AND FORGINGS 1.8Ni - 0.25Mo (0.38 - 0.43C) (4640) Heat Treated@ 125@ 000 psi (860 MPa) Tensile Strength
• 1978 SAE AMS6317D-1978 STEEL BARS AND FORGINGS 1.8Ni - 0.25Mo (0.38 - 0.43C) (4640) Heat Treated@ 125@ 000 psi (862 MPa) Tensile Strength
• 1971 SAE AMS6317C-1971 STEEL BARS AND FORGINGS 1.8Ni - 0.25Mo (0.38 - 0.43C) (4640) Heat Treated@ 125@ 000 psi (862 MN/m2) Tensile Strength
• 1945 SAE AMS6317B-1945 STEEL 1.8 Ni - .25 Mo (.38 - .43c) Heat Treated (125@ 000 TS)
• 1942 SAE AMS6317A-1942 STEEL Nickel Molybdenum
• 1939 SAE AMS6317-1939 STEEL Nickel Molybdenum