SAE AMS3267/2A-1992
Sealing Compound, Low Adhesion, Corrosion Inhibiting 9,000 to 14,000 Poises (900 to 1400 Pa.s), 1/2 Hour Application Time (B-1/2)
- Standard No.
- SAE AMS3267/2A-1992
- Release Date
- 1992
- Published By
- Society of Automotive Engineers (SAE)
- Latest
- SAE AMS3267/2A-1992
- Scope
- This specification covers accelerated curing synthetic rubber compounds with corrosion inhibitors and low adhesive strength supplied as a two-component system. This product has been used typically for sealing aircraft access doors and accessories where gaskets are required, but usage is not limited to such applications. Compound is classified as a B-1/2 sealing compound; the compound being suitable for application by an extrusion gun or spatula with a minimum application time of 1/2 hour after mixing.
SAE AMS3267/2A-1992 Referenced Document
- SAE AMS2825A-1987 Material Safety Data Sheets
- SAE AMS3180 TOLUENE THINNER Commercial
- SAE AMS4049H-1987 Aluminum Alloy Sheet and Plate@ Alclad 5.6Zn - 2.5Mg - 1.6Cu - 0.23Cr (Alclad 7075; -T6 Sheet - T651 Plate) Solution and Precipitation Heat Treated (UNS A97075)
SAE AMS3267/2A-1992 history
- 1992 SAE AMS3267/2A-1992 Sealing Compound, Low Adhesion, Corrosion Inhibiting 9,000 to 14,000 Poises (900 to 1400 Pa.s), 1/2 Hour Application Time (B-1/2)
SAE AMS3267/2A-1992 -All Parts
SAE AMS3267-1984 SEALING COMPOUND, LOW ADHESION, CORROSION INHIBITING For Removable Panels and Fuel Tank Inspection Plates
SAE AMS3267/1-1992 SEALING COMPOUND, LOW ADHESION, CORROSION INHIBITING 200 - 600 Poises (20 - 60 Pa·s), 1/2 Hour Application Time (A-1/2)
SAE AMS3267/1A-2003 SEALING COMPOUND, LOW ADHESION, CORROSION INHIBITING 200 to 600 Poises (20 to 60 Pa·s), 1/2 Hour Application Time (A-1/2)
SAE AMS3267/2-1992 SEALING COMPOUND, LOW ADHESION, CORROSION INHIBITING 9,000 - 14,000 Poises (900 - 1400 Pa·s), 1/2 Hour Application Time (B-1/2)
SAE AMS3267/2A-1992 Sealing Compound, Low Adhesion, Corrosion Inhibiting 9,000 to 14,000 Poises (900 to 1400 Pa.s), 1/2 Hour Application Time (B-1/2)
SAE AMS3267/2B-2003 Sealing Compound, Low Adhesion, Corrosion Inhibiting, 9,000 to 14,000 Poises (900 to 1400 Pa⋅s), 1/2 Hour Application Time (B-1/2)
SAE AMS3267/3-1992 SEALING COMPOUND, LOW ADHESION, CORROSION INHIBITING 200 - 600 Poises (20 - 60 Pa·s), 2 Hour Application Time (A-2)
SAE AMS3267/3A-1992 Sealing Compound@ Low Adhesion@ Corrosion Inhibiting 200 to 600 Poises (20 to 60 Pa.s)@ 2 Hour Application Time (A-2)
SAE AMS3267/3B-2011 Sealing Compound@ Low Adhesion@ Corrosion Inhibiting 200 to 600 Poises (20 to 60 Pa?s)@ 2 Hour Application Time (A-2)
SAE AMS3267/4-1992 SEALING COMPOUND, LOW ADHESION, CORROSION INHIBITING 9,000 - 14,000 Poises (900 - 1400 Pa·s), 2 Hour Application Time (B-2)
SAE AMS3267/4A-1992 Sealing Compound, Low Adhesion, Corrosion Inhibiting 9,000 to 14,000 Poises (900 to 1400 Pa.s), 2 Hour Application Time (B-2)
SAE AMS3267/4B-2003 Sealing Compound, Low Adhesion, Corrosion Inhibiting, 9,000 to 14,000 Poises (900 to 1400 Pa⋅s), 2 Hour Application Time (B-2)
SAE AMS3267A-1992 Sealing Compound, Low Adhesion, Corrosion Inhibiting for Removable Panels and Fuel Tank Inspection Plates
SAE AMS3267B-2004 Sealing Compound@ Low Adhesion@ Corrosion Inhibiting for Removable Panels and Fuel Tank Inspection Plates