SAE AS4959-1997 PDF

Scope: This procurement specification covers bolts and screws made from a corrosion and heat resistant, age hardenable iron base alloy of the type identified under the Unifief Numbering Systems as UNS S66286. The following specification designations and their properties are covered: AS4959 140 ksi minimum ultimate tensile strength at room temperature 70 ksi stress-rupture strength at 1200 degrees F; AS4959-1 140 ksi minimum ultimate tensile strength at room temperature 84 ksi minimum ultimate shear strength at room temperature.

SAE AS4959-1997 Referenced Document

ASTM D1417-97 Standard Test Methods for Rubber Latices-Synthetic
ASTM D3951-95 Standard Practice for Commercial Packaging
ISO 3161:1996 Aerospace - UNJ threads, with controlled root radius, for aerospace - Inch series
ISO 9001:1994 Quality systems - Model for quality assurance in design, development, production, installation and servicing
ISO 9002:1994 Quality systems - Model for quality assurance in production, installation and servicing
SAE AMS2759/3B-1996 Heat Treatment Precipitation-Hardening Corrosion-Resistant and Maraging Steel Parts
SAE AMS5734H-1995 Steel@ Corrosion and Heat Resistant@ Bars@ Wire@ Forgings@ and Tubing 15Cr - 25.5Ni - 1.2Mo - 2.1Ti - 0.006B - 0.30V Consumable Electrode Melted@ 1650 Degrees F (899 Degrees C) Solution Heat Treated (UNS S66286)
SAE AS1132E-1996 Bolts@ Screws and Nuts - External Wrenching UNJ Thread@ Inch Series - Design Standard
SAE AS3062C-1979 Bolts, Screws and Studs, Screw Thread Requirements
SAE AS3063B-1996 Bolts, Screws, and Studs, Geometric Control Requirements

2018 SAE AS4959A-2018 Bolts and Screws@ Steel@ UNS S66286 Tensile Strength 140 ksi 1650 °F Solution Heat Treatment Aged Before Fillet and Thread Rolling Procurement Specification
2012 SAE AS4959-2012 Bolts and Screws, Steel, UNS S66286 Tensile Strength 140 ksi 1650 °F Solution Heat Treatment Aged Before Fillet and Thread Rolling Procurement Specification
1997 SAE AS4959-1997 Bolts and Screws, Steel, UNS S66286 Tensile Strength 140 ksi 1650 °F Solution Heat Treatment Aged Before Fillet and Thread Rolling Procurement Specification