SAE AMS4761A-1999 PDF

Scope: This specification covers a silver alloy in the form of wire, rod, sheet, strip, foil, pig, powder, shot, and chips, and a viscous mixture (paste) of powder in a suitable binder. This material has been used typically for joining ferrous metals and alloys, requiring good joint strength up to 600 degrees F (316 degrees C) for short-time service or up to 400 degrees F (204 degrees C) for long-time service, and for joining nonferrous metals except those having base of aluminum or magnesium, but usage is not limited to such applications.

SAE AMS4761A-1999 Referenced Document

ASTM B214-99 Standard Test Method for Sieve Analysis of Metal Powders*， 1999-04-10 Update
ASTM E56-90
SAE AMS2222 TOLERANCES Copper and Copper Alloy Plate@ Sheet and Strip
SAE AMS2222H-1994 Tolerances, Copper and Copper Alloy Sheet, Strip, and Plate
SAE AMS2224 Tolerances Copper and Copper Alloy Wire
SAE AMS2224F-1993 Tolerances, Copper and Copper Alloy Wire
SAE MAM2222 Tolerances@ Metric Copper and Copper Alloy Sheet@ Strip@ and Plate
SAE MAM2224 TOLERANCES, METRIC Copper and Copper Alloy Wire

2021 SAE AMS4761C-2021 Silver Alloy, Brazing Filler Metal 38Ag - 32Cu - 28Zn - 2.0Sn 1200 to 1330 °F (649 to 721 °C) Solidus-Liquidus Range (UNS P07380)
2015 SAE AMS4761B-2015 Silver Alloy@ Brazing Filler Metal 38Ag �C 32Cu �C 28Zn �C 2.0Sn 1200 to 1330 ��(649 to 721 �� Solidus-Liquidus Range (UNS P07380)
2009 SAE AMS4761A-2009 Silver Alloy, Brazing Filler Metal 38Ag - 32Cu - 28Zn - 2.0Sn 1200 to 1330 °F (649 to 721 °C) Solidus-Liquidus Range
1999 SAE AMS4761A-1999 Silver Alloy Brazing Filler Metal 38Ag 32Cu 28Zn 2.0Sn 1200 to 1330°F (649 to 721°C) Solidus-Liquidus Range
1992 SAE AMS4761-1992 Silver Alloy Brazing Filler Metal 38Ag - 32Cu - 28Zn - 2.0Sn 1200 to 1330 Degrees F (649 to 721 Degrees C) Solidus- Liquidus Range (UNS P07380)