SAE AMS5344D-1994
Steel, Corrosion Resistant, Investment Castings 16Cr 4.1Ni 0.28Cb 3.2Cu Homogenization, Solution and Precipitation Heat Treated 180 ksi (1241 MPa) Tensile Strength

Standard No.

SAE AMS5344D-1994

Release Date

1994

Published By

Society of Automotive Engineers (SAE)

Status

Withdraw

Replace By

SAE AMS5344D-2000

Latest

SAE AMS5344G-2019

Scope

This specification covers a corrosion-resistant steel in the form of investment castings. These castings have been used typically for parts requiring good corrosion resistance and strength up to 600 degrees F (316 degrees C), but usage is not limited to such applications. Certain processing procedures and service conditions may cause these castings to become subject to stress-corrosion cracking. APR1110 recommends practices to minimize such conditions.

SAE AMS5344D-1994 history

• 2019 SAE AMS5344G-2019 Steel, Corrosion-Resistant, Investment Castings 16Cr - 4.1Ni - 0.28Cb - 3.2Cu Homogenization, Solution, and Precipitation Heat Treated (H900) 180 ksi (1241 MPa) Tensile Strength (17-4)
• 2013 SAE AMS5344F-2013 Steel, Corrosion-Resistant, Investment Castings 16Cr - 4.1Ni - 0.28Cb - 3.2Cu Homogenization, Solution, and Precipitation Heat Treated (H900) 180 ksi (1241 MPa) Tensile Strength (17-4)
• 2007 SAE AMS5344F-2007 (R) Steel, Corrosion-Resistant, Investment Castings 16Cr - 4.1Ni - 0.28Cb - 3.2Cu Homogenization, Solution, and Precipitation Heat Treated (H900) 180 ksi (1241 MPa) Tensile Strength (17-4) UNS J92180 and J92200
• 2006 SAE AMS5344E-2006 Steel@ Corrosion-Resistant@ Investment Castings 16Cr - 4.1Ni - 0.28Cb - 3.2Cu Homogenization@ Solution@ and Precipitation Heat Treated (H900) 180 ksi (1241 MPa) Tensile Strength (UNS J92180 and J92200)
• 2000 SAE AMS5344D-2000 Steel, Corrosion Resistant, Investment Castings 16Cr - 4.1Ni - 0.28Cb - 3.2Cu Homogenization, Solution, and Precipitation Heat Treated (H900) 180 ksi (1241 MPa) Tensile Strength
• 1994 SAE AMS5344D-1994 Steel, Corrosion Resistant, Investment Castings 16Cr 4.1Ni 0.28Cb 3.2Cu Homogenization, Solution and Precipitation Heat Treated 180 ksi (1241 MPa) Tensile Strength
• 1989 SAE AMS5344C-1989 Steel Castings@ Investment@ Corrosion Resistant 16Cr - 4.1Ni - 0.28(Cb+Ta) - 3.2Cu Solution and Precipitation Heat Treated 180@000 psi (1241 MPa) Tensile Strength (UNS J92200)
• 1985 SAE AMS5344B-1985 STEEL CASTINGS, INVESTMENT, CORROSION RESISTANT 16Cr - 4.1Ni - 0.28(Cb+Ta) - 3.2Cu Solution and Precipitation Heat Treated 180,000 psi (1240 MPa) Tensile Strength
• 1978 SAE AMS5344A-1978 STEEL CASTINGS, INVESTMENT, CORROSION RESISTANT 16Cr - 4.1Ni - 0.28(Cb+Ta) - 3.2Cu Solution and Precipitation Heat Treated 180,000 psi (1241 MPa) Tensile Strength
• 1963 SAE AMS5344-1963 STEEL CASTINGS, INVESTMENT, CORROSION RESISTANT 16Cr - 4.0Ni - 3.1Cu Solution and Precipitation Heat Treated, 180,000 psi Premium Quality