1.1 This test method covers evaluation of the ferrous corrosion control characteristics of water–miscible metalworking fluids.
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.
1.2.1 Exception—Note 1 contains inch-pound units since the drill sizes and feed rates do not have readily available metric equivalents.
1.2.2 Exception—U.S. Standard sieve sizes include mesh values.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
ASTM D4627-22 Referenced Document
ASTM D4175 Standard Terminology Relating to Petroleum Products, Liquid Fuels, and Lubricants*, 2023-07-01 Update
ASTM D4627-22 history
2022ASTM D4627-22 Standard Test Method for Iron Chip Corrosion for Water–Miscible Metalworking Fluids
2017ASTM D4627-12(2017) Standard Test Method for Iron Chip Corrosion for Water–Miscible Metalworking Fluids
2012ASTM D4627-12 Standard Test Method for Iron Chip Corrosion for Waterndash;Miscible Metalworking Fluids
1992ASTM D4627-92(2007) Standard Test Method for Iron Chip Corrosion for Water-Dilutable Metalworking Fluids
1992ASTM D4627-92(2002) Standard Test Method for Iron Chip Corrosion for Water8212;Dilutable Metalworking Fluids
1997ASTM D4627-92(1997) Standard Test Method for Iron Chip Corrosion for Water-Dilutable Metalworking Fluids